Hexcel® HexPly® F522 Epoxy Resin, W3C282 Carbon Fabric
| Category | Polymer , Thermoset , Carbon Fiber/Thermoset Composite , Epoxy , Epoxy/Carbon Fiber Composite |
| Manufacturer | Hexcel |
| Trade Name | HexPly® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Hexcel® HexPly® F522 Epoxy Resin, W3C282 Carbon Fabric.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Hexcel designation: TW3C282-42"-F522; Fiber: Toho® G30/500-3KInformation provided by HexCel
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 745 MPa @Temperature -55.0 °C |
108000 psi @Temperature -67.0 °F |
Dry |
| 855 MPa @Temperature 24.0 °C |
124000 psi @Temperature 75.2 °F |
Dry | |
| 855 MPa @Temperature 71.0 °C |
124000 psi @Temperature 160 °F |
Dry | |
| Tensile Modulus | 62.7 GPa @Temperature 71.0 °C |
9090 ksi @Temperature 160 °F |
Dry |
| 63.4 GPa @Temperature 24.0 °C |
9200 ksi @Temperature 75.2 °F |
Dry | |
| 64.8 GPa @Temperature -55.0 °C |
9400 ksi @Temperature -67.0 °F |
Dry | |
| Flexural Yield Strength | 276 MPa | 40000 psi | Long Beam, dry |
| Compressive Yield Strength | 400 MPa @Temperature 71.0 °C |
58000 psi @Temperature 160 °F |
Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) |
| 655 MPa @Temperature 24.0 °C |
95000 psi @Temperature 75.2 °F |
Dry | |
| Compressive Modulus | 59.3 GPa @Temperature 71.0 °C |
8600 ksi @Temperature 160 °F |
Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) |
| 64.1 GPa @Temperature 24.0 °C |
9300 ksi @Temperature 75.2 °F |
Dry | |
| Bearing Yield Strength | 848 MPa @Temperature 24.0 °C |
123000 psi @Temperature 75.2 °F |
Dry |
| Shear Strength | 26.2 MPa @Temperature 71.0 °C |
3800 psi @Temperature 160 °F |
Short Beam, Wet (14 ± 1/2 days of water immersion at 160 ± 5°F (71 ± 3°C) |
| 60.0 MPa @Temperature 24.0 °C |
8700 psi @Temperature 75.2 °F |
Short Beam, Jet Fuel (30 ± 1 days of Jet A Fuel (ASTM D1655) at 75 ± 5°F (24 ± 3°C) | |
| 61.0 MPa @Temperature 24.0 °C |
8850 psi @Temperature 75.2 °F |
Short Beam, Dry | |
| 61.4 MPa @Temperature 24.0 °C |
8910 psi @Temperature 75.2 °F |
Short Beam, Skydrol (30 ± 1 days of Type 2 Skydrol Hydraulic Fluid at 140 ± 5°F (60 ± 3°C) |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Dry Resin Content (%) | 37-41 | Prepreg |
| Fiber Volume (%) | 0.02 | Laminate |
| Flow (%) | 8-20 | |
| Wet Resin Content (%) | 52 | Laminate |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® 943X PC Copolymer (Asia Pacific)
- LATI Latamid 6 H2 G/20-V2HF PA 6, 20% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- DuPont Bynel® 4105 Anhydride-Modified LLDPE Adhesive Resin
- Zircar Refractory Composites RSPA-SOL3 Silica-Magnesia, Non-RCF Paper
- Dow DNDA-1149 NT 7 Linear Low Density Polyethylene Resin
- EMS-Grivory Grivory® BGZ-30 PA6-GF30
- E-Polymers TEKAMID® H12T Unreinforced High Impact PA/ABS Alloy
- Ascend Performance Materials Vydyne® R533T Nylon 66, Translucent, 33% Glass Filled, Conditioned (2.5% Moisture)
- Chevron Phillips MarFlex® 9608XD HDPE Film Grade
Copyright © lookpolymers.com All Rights Reserved