Techmer ES ElastoblendÂ® PA6/66 IM3 BK

Category	Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, Unreinforced
Manufacturer	Techmer ES
Trade Name	Elastoblend®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Techmer ES ElastoblendÂ® PA6/66 IM3 BK.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Lubricant and Impact ModifierFeatures: Copolymer, Heat Stabilized, Lubricant and Impact ModifiedProcessing Method: Injection MoldingInformation provided by TP Composites, Inc.

Physical Properties	Metric	English	Comments
Density	1.09 g/cc	0.0394 lb/inÂ³	ASTM D792
Water Absorption	1.8 % @Time 86400 sec	1.8 % @Time 24.0 hour	ASTM D570
Linear Mold Shrinkage, Flow	0.016 cm/cm @Thickness 3.17 mm	0.016 in/in @Thickness 0.125 in	ASTM D955

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	111	111	ASTM D785
Tensile Strength	60.7 MPa	8800 psi	ASTM D638
Elongation at Yield	50 %	50 %	ASTM D638
Flexural Yield Strength	82.7 MPa	12000 psi	ASTM D790
Flexural Modulus	2.65 GPa	385 ksi	ASTM D790
Izod Impact, Notched	1.33 J/cm @Thickness 3.17 mm, Temperature -40.0 Â°C	2.50 ft-lb/in @Thickness 0.125 in, Temperature -40.0 Â°F	ASTM D256
	6.41 J/cm @Thickness 3.17 mm, Temperature 22.8 Â°C	12.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 Â°F	ASTM D256
Izod Impact, Unnotched	NB @Thickness 3.17 mm	NB @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	79.2 Âµm/m-Â°C	44.0 Âµin/in-Â°F	ASTM D696
Deflection Temperature at 0.46 MPa (66 psi)	204 Â°C	400 Â°F	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	60.0 Â°C	140 Â°F	Unannealed; ASTM D648