Lubrizol Estane® 2103-80AE Thermoplastic Polyurethane Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Lubrizol (former Noveon) |
| Trade Name | ESTANE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lubrizol Estane® 2103-80AE Thermoplastic Polyurethane Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Formerly PellethaneAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 - 0.0080 cm/cm | 0.0060 - 0.0080 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | -0.00200 - 0.0050 cm/cm | -0.00200 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 40 g/10 min @Load 1.20 kg, Temperature 224 °C |
40 g/10 min @Load 2.65 lb, Temperature 435 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 82 | 82 | ASTM D2240 |
| Tensile Strength, Ultimate | 34.5 MPa | 5000 psi | ASTM D412 |
| Elongation at Break | 600 % | 600 % | ASTM D412 |
| 50% Modulus | 0.00414 GPa | 0.600 ksi | ASTM D412 |
| 100% Modulus | 0.00550 GPa | 0.798 ksi | ASTM D412 |
| 300% Modulus | 0.0117 GPa | 1.70 ksi | ASTM D412 |
| Tear Strength | 105 kN/m | 599 pli | Die C; ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 20 | 20 | H22 Wheel, 1000g; ASTM D1044 |
| Compression Set | 30 % @Temperature 25.0 °C, Time 79200 sec |
30 % @Temperature 77.0 °F, Time 22.0 hour |
ASTM D395, Method B |
| 33 % @Temperature 70.0 °C, Time 79200 sec |
33 % @Temperature 158 °F, Time 22.0 hour |
ASTM D395, Method B | |
| Tensile Set | 70 % | 70 % | Elongation set after break; ASTM D412 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 168 µm/m-°C @Temperature 20.0 °C |
93.3 µin/in-°F @Temperature 68.0 °F |
ASTM D969 |
| Vicat Softening Point | 85.0 °C | 185 °F | 120°C/hr, 9.8N; ASTM D1525 |
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 199 °C | 360 - 390 °F | Extrusion |
| 182 - 210 °C | 360 - 410 °F | Molding | |
| Mold Temperature | 16.0 - 60.0 °C | 60.8 - 140 °F | |
| Drying Temperature | 82.0 - 93.0 °C | 180 - 199 °F | air dew point <-40°C |
Users viewing this material also viewed the following:
- RheTech Products G13P100-332UV 13% Glass Fiber Reinforced Polypropylene, UV Stabilized, (GM 9772) Light Neutral
- Solvay Specialty Polymers Amodel® AF-1550 V0 Polyphthalamide (PPA) Resin, 50% Glass/Mineral Reinforced, Dry As Molded &
- Indium Corp. Indalloy 86 Bismuth-Cadmium Solder Alloy
- SABIC Innovative Plastics LNP THERMOCOMP UX06028 PPA (Europe-Africa-Middle East)
- Techmer ES Luriblend® PES GF30 TL15 30% Glass Filled
- A. Schulman POLYBATCH™ Gardenia P80515PF Concentrate Based In Polypropylene
- A. Schulman POLYBATCH™ FSU-105 Concentrate Based In LDPE
- DSM Stanyl® TW241F10 Nylon 46-50% Glass Reinforced (European Grade) (Cond)
Copyright © lookpolymers.com All Rights Reserved