Unitika AXG-1500-300 Dry

Category Polymer , Thermoplastic , Polyarylate
Manufacturer Unitika
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Unitika AXG-1500-300 Dry.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Characteristics: Glass-reinforced grades of the AX1500 resin, excellent in heat and chemical resistancesFavorable rigidity and dimensional accuracyInformation provided by Unitika Ltd.
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ASTM D792
Water Absorption 0.60 %

@Thickness 3.17 mm,
Time 86400 sec
0.60 %

@Thickness 0.125 in,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage, Flow 0.0035 cm/cm

@Thickness 3.00 mm
0.0035 in/in

@Thickness 0.118 in
Linear Mold Shrinkage, Transverse 0.0070 cm/cm

@Thickness 3.00 mm
0.0070 in/in

@Thickness 0.118 in
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength at Break 143 MPa
20700 psi
ASTM D638
Elongation at Break 4.0 %
4.0 %
ASTM D638
Flexural Strength 211 MPa
30600 psi
ASTM D790
Flexural Modulus 8.20 GPa
1190 ksi
ASTM D790
Compressive Strength 147 MPa
21300 psi
ASTM D695
Izod Impact, Notched 0.760 J/cm

@Thickness 3.17 mm
1.42 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 46.0 µm/m-°C
25.6 µin/in-°F
ASTM D696
Deflection Temperature at 1.8 MPa (264 psi) 179 °C
354 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 210 - 230 °C
410 - 446 °F
Middle Barrel Temperature 240 - 260 °C
464 - 500 °F
Front Barrel Temperature 250 - 270 °C
482 - 518 °F
Nozzle Temperature 250 - 270 °C
482 - 518 °F
Mold Temperature 80.0 - 120 °C
176 - 248 °F
actual surface temp
Drying Temperature 100 °C
212 °F
Dry Time 10.0 - 24.0 hour
10.0 - 24.0 hour
Back Pressure 0.490 - 1.47 MPa
71.1 - 213 psi
gage pressure