Sumitomo Bakelite North America RX® 3-1-530-P Long-Glass Reinforced Diallyl Phthalate
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Long Glass Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America RX® 3-1-530-P Long-Glass Reinforced Diallyl Phthalate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Long glass fiber reinforced, flame retardant, diallyl ortho-phthalate molding compound which meets the requirements of ASTM D5948 Type GDI-30F.Information provided by Vyncolit, a Sumitomo Bak Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in³ | Relative Density; ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | Compression Molding; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | At Rupture; ASTM D790 |
| Flexural Modulus | 20.0 GPa | 2900 ksi | ASTM D790 |
| Compressive Strength | 140 MPa | 20300 psi | ASTM D695 |
| Izod Impact, Notched | 1.70 J/cm | 3.18 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature 20.0 °C |
12.2 µin/in-°F @Temperature 68.0 °F |
ASTM E-831 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | UL 746B |
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | As molded; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
|
| Oxygen Index | 30 % | 30 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.5 @Frequency 1e+6 Hz |
3.5 @Frequency 1e+6 Hz |
Wet; ASTM D150 |
| 4.1 @Frequency 1000 Hz |
4.1 @Frequency 1000 Hz |
wet; ASTM D150 | |
| Dielectric Strength | 13.4 kV/mm | 340 kV/in | 60Hz, Step-by-Step, wet; ASTM D149 |
| Dissipation Factor | 0.010 @Frequency 1000 Hz |
0.010 @Frequency 1000 Hz |
wet; ASTM D150 |
| 0.018 @Frequency 1e+6 Hz |
0.018 @Frequency 1e+6 Hz |
wet; ASTM D150 | |
| Arc Resistance | 130 sec | 130 sec | ASTM D495 |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black, Gray, Green | |
| Flammability: Burning, sec | 40 | ASTM D229 |
| Flammability: Ignition, sec | 110 | ASTM D229 |
| Form | Coarse Flake | |
| Main Filler | Glass Fiber | |
| Molding Method | Compression, transfer |
Users viewing this material also viewed the following:
- Overview of materials for PETG Copolyester
- Huntsman AVALON® 90 AKU Thermoplastic Polyurethane
- ChevronTexaco Multigear® LS SAE 80W-90
- Diamond Polymers NPP30-1200S Homopolymer Polypropylene
- China-Yixing Longly Refractories Plate Corundum-Mullite
- PolyOne Synprene® RT-3830E Thermoplastic Elastomer - SBC (discontinued **)
- Huntsman PE1158 EVA Film Extrusion (discontinued **)
- Dow Advanta® 3650 Specialty Elastomer (discontinued **)
- DuPont Performance Polymers Hypalon® 40 Chlorosulfonated Polyethylene Rubber, Gum Compound (discontinued **)&
Copyright © lookpolymers.com All Rights Reserved