SABIC Innovative Plastics LNP Thermocomp DF0066P PC

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP THERMOCOMP
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	SABIC Innovative Plastics LNP Thermocomp DF0066P PC.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

LNP THERMOCOMP* DF0066P is a compound based on Polycarbonate resin containing Glass Fiber, Flame Retardant. Added features of this material include: Exceptional Processing.This data was supplied by SABIC-IP for the Americas region.

Physical Properties	Metric	English	Comments
Density	1.446 g/cc	0.05224 lb/inÂ³	ASTM D 792
Linear Mold Shrinkage, Flow	0.0015 cm/cm <br>@Time 86400 sec	0.0015 in/in <br>@Time 24.0 hour	ASTM D 955
Linear Mold Shrinkage, Transverse	0.0035 cm/cm <br>@Time 86400 sec	0.0035 in/in <br>@Time 24.0 hour	ASTM D 955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	119 MPa	17300 psi	ASTM D 638
Elongation at Break	5.0 %	5.0 %	ASTM D 638
Flexural Strength	180 MPa	26100 psi	ASTM D 790
Flexural Modulus	8.61 GPa	1250 ksi	ASTM D 790
Izod Impact, Notched	1.06 J/cm <br>@Temperature 23.0 Â°C	1.99 ft-lb/in <br>@Temperature 73.4 Â°F	ASTM D 256
Izod Impact, Unnotched	7.41 J/cm <br>@Temperature 23.0 Â°C	13.9 ft-lb/in <br>@Temperature 73.4 Â°F	ASTM D 4812
Impact Test	11.0 J <br>@Temperature 23.0 Â°C	8.11 ft-lb <br>@Temperature 73.4 Â°F	Instrumented Impact Energy @ peak; ASTM D 3763

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	141 Â°C <br>@Thickness 3.20 mm	286 Â°F <br>@Thickness 0.126 in	unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi)	136 Â°C <br>@Thickness 3.20 mm	277 Â°F <br>@Thickness 0.126 in	unannealed; ASTM D 648