Styron Pulse® EXT 100 ABS + Polycarbonate
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® EXT 100 ABS + Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PULSE® EXT 100 Engineering resin has been designed to provide excellent processability, high heat resistance, and high impact strength at both room and low temperatures. PULSE EXT100 Engineering resin has been used in automotive exterior trim applications.Data provided by Dow Chemical.This product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM Data |
| Melt Density | 1.02 g/cc | 0.0368 lb/in³ | Melt density |
| Water Absorption | 0.15 % | 0.15 % | |
| Moisture Absorption at Equilibrium | 0.32 % | 0.32 % | Humidity Absorption |
| Linear Mold Shrinkage | 0.0070 cm/cm | 0.0070 in/in | |
| Melt Flow | 2.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
2.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM Data |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | |
| Tensile Strength, Ultimate | 48.3 MPa | 7010 psi | ASTM Data |
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM Data |
| Elongation at Break | 100 % | 100 % | ASTM Data |
| Elongation at Yield | 4.8 % | 4.8 % | ISO Data |
| Tensile Modulus | 2.10 GPa | 305 ksi | ISO Data. |
| Izod Impact, Notched | 6.41 J/cm | 12.0 ft-lb/in | ASTM Data |
| 5.34 J/cm @Temperature -50.0 °C |
10.0 ft-lb/in @Temperature -58.0 °F |
ASTM Data | |
| Charpy Impact Unnotched | NB | NB | ISO Data |
| NB | NB | ISO Data, Low Temp | |
| Charpy Impact, Notched | 2.40 J/cm² | 11.4 ft-lb/in² | ISO Data, Low Temp |
| 6.10 J/cm² | 29.0 ft-lb/in² | ISO Data | |
| Impact Test | 50.9 J @Temperature -30.0 °C |
37.5 ft-lb @Temperature -22.0 °F |
Instrumented Dart Total Energy |
| 50.9 J @Temperature 23.0 °C |
37.5 ft-lb @Temperature 73.4 °F |
Instrumented Dart Total Energy |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 20.0 °C |
38.9 µin/in-°F @Temperature 68.0 °F |
ASTM data |
| Specific Heat Capacity | 1.98 J/g-°C | 0.473 BTU/lb-°F | |
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 132 °C | 270 °F | Unannealed; ASTM Data |
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | Unannealed; ASTM Data |
Users viewing this material also viewed the following:
- Plansee Ta2.5W Tantalum-Tungsten 2.5 Alloy
- RheTech Products FT3080-729UV Thermoplastic Polyolefin, UV Stabilized, AG-64 Grey
- GEHR Plastics PPSU Polyphenylenesulfone
- LATI Latiohm 83-07 PD11 CNT PA12, Impact Modified
- Solvay Specialty Polymers Polidiemme® G/440 Thermoset Elastomer (TSE)
- SABIC Innovative Plastics LNP THERMOCOMP RF006S PA 66 (Asia Pacific)
- A. Schulman POLYBATCH™ Canyon 10290U/4 Concentrate Based In LLDPE
- Formosa Plastics Formolene® 4142T Injection Molding Polypropylene
- Covestro Bayfill® 370 Polyurethane Semi-Rigid Foam, Polymeric Catalyst, Closed Pour, MDI-based 2-Component Liquid System
- NOVA Chemicals Sclair® 35BPM MDPE Extrusion Resin, 2.2% Carbon Black Filled (discontinued **)
Copyright © lookpolymers.com All Rights Reserved