Styron Pulse® 2200BG ABS + PC
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® 2200BG ABS + PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Water Absorption | 0.53 % | 0.53 % | 23°C, 24hrs; ASTM D570 |
| Linear Mold Shrinkage | >= 0.0060 cm/cm | >= 0.0060 in/in | ASTM D955 |
| Melt Flow | 4.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 52.7 MPa | 7650 psi | ASTM D638 |
| Tensile Strength, Yield | 53.8 MPa | 7800 psi | ASTM D638 |
| Elongation at Break | 115 % | 115 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.28 GPa | 330 ksi | ASTM D638 |
| Flexural Strength | 83.4 MPa | 12100 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 4.00 J/cm | 7.50 ft-lb/in | -20°F; ASTM D256 |
| 6.94 J/cm | 13.0 ft-lb/in | 73°F; ASTM D256 | |
| Dart Drop, Total Energy | 53.0 J @Temperature 22.8 °C |
39.1 ft-lb @Temperature 73.0 °F |
ASTM D3763 |
| 54.0 J @Temperature -28.9 °C |
39.8 ft-lb @Temperature -20.0 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 72.0 µm/m-°C @Temperature -40.0 - 82.2 °C |
40.0 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 265 °F | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | unannealed; ASTM D648 |
| Vicat Softening Point | 144 °C | 291 °F | ASTM D1525 |
Users viewing this material also viewed the following:
- Oxford Polymers 604-I Polycarbonate/Polybutylene Terephthalate (PBT) Alloy
- PTS PBT-20GFR 20% Glass Filled
- NOVA Chemicals Sclair® 58G (High Gloss) HDPE Blow Molding Resin (discontinued **)
- Total Lacqtene® 1003 FE 30 HDPE, blow molding (discontinued **)
- Imerys 160D Ground Mica
- Gouda Vuurvast VIBRON 160 H Dense Vibrating Refractory Castable
- Techmer ES HiFill FR® PA6/6 GF33 FR HS L 33% Glass Filled
- Goodfellow Molybdenum 80/Titanium 20 Alloy
- BASF Ultramid® 8231G HS BK-102 14% Glass Filled PA6 (Dry)
- Arlon 30580R015 0.015" (0.381 mm) Uncured Unsupported Silicone Rubber on Kodacel Carrier
Copyright © lookpolymers.com All Rights Reserved