Lanxess Durethan® BKV 135 DUS008 000000 Nylon 6, 35% Glass Fiber

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 40% Glass Fiber Filled , Nylon 6, Glass Filled, Impact Grade
Manufacturer Lanxess
Trade Name Durethan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® BKV 135 DUS008 000000 Nylon 6, 35% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, 35% glass fibers, injection molding, impact modifiedInformation provided by LANXESS.
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
conditioned, 5 mm/min; ISO 527-1,-2
170 MPa
24700 psi
5 mm/min; ISO 527-1,-2
Elongation at Break 3.0 %
3.0 %
5 mm/min; ISO 527-1,-2
7.0 %
7.0 %
conditioned, 5 mm/min; ISO 527-1,-2
Tensile Modulus 6.00 GPa
870 ksi
conditioned, 1 mm/min; ISO 527-1,-2
10.2 GPa
1480 ksi
1 mm/min; ISO 527-1,-2
Flexural Strength 170 MPa
24700 psi
conditioned, 2 mm/min; ISO 178-A
280 MPa
40600 psi
2 mm/min; ISO 178-A
Flexural Modulus 5.50 GPa
798 ksi
conditioned, 2 mm/min; ISO 178-A
9.10 GPa
1320 ksi
2 mm/min; ISO 178-A
Charpy Impact Unnotched 8.50 J/cm²

@Temperature -30.0 °C
 40.4 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eU
8.50 J/cm²

@Temperature -30.0 °C
 40.4 ft-lb/in²

@Temperature -22.0 °F
 conditioned; ISO 179-1eU
10.0 J/cm²

@Temperature 23.0 °C
 47.6 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eU
11.0 J/cm²

@Temperature 23.0 °C
 52.3 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 179-1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 ISO 179-1eA
1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 conditioned; ISO 179-1eA
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 ISO 179-1eA
3.00 J/cm²

@Temperature 23.0 °C
 14.3 ft-lb/in²

@Temperature 73.4 °F
 conditioned; ISO 179-1eA
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 210 °C
410 °F
ISO 75-1,-2
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75-1,-2
Processing Properties Metric English Comments
Dry Time 2.00 - 6.00 hour

@Temperature 80.0 °C
 2.00 - 6.00 hour

@Temperature 176 °F
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
Karl Fischer test