Styron Pulse® 2100LG ABS + PC
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® 2100LG ABS + PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 23°C, 24hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 4.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
4.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 53.8 MPa | 7800 psi | ASTM D638 |
| Tensile Strength, Yield | 53.1 MPa | 7700 psi | ASTM D638 |
| Elongation at Break | 125 % | 125 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.21 GPa | 320 ksi | ASTM D638 |
| Flexural Strength | 80.7 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | -20°F; ASTM D256 |
| 6.41 J/cm | 12.0 ft-lb/in | 73°F; ASTM D256 | |
| Dart Drop, Total Energy | 57.0 J @Temperature 22.8 °C |
42.0 ft-lb @Temperature 73.0 °F |
ASTM D3763 |
| 62.0 J @Temperature -28.9 °C |
45.7 ft-lb @Temperature -20.0 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 73.8 µm/m-°C @Temperature -40.0 - 82.2 °C |
41.0 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 265 °F | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | unannealed; ASTM D648 |
| Vicat Softening Point | 143 °C | 290 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 25 % | 25 % | Gardner Gloss, 60° smooth; ASTM D542 |
Users viewing this material also viewed the following:
- Raschig Group EPOXIDUR® 3581 T-1 EP Epoxy, Molded, Glass Fiber Filler
- Solvay Specialty Polymers Ixef® 1028 Polyarylamide (PARA) (discontinued **)
- SABIC Innovative Plastics Xenoy® HX6600HP PBT+PC
- Techmer ES Plastiblend® PA6/10 BK Nylon 610
- Master Bond EP21TDC Toughened, Shock Resistant Two Component Epoxy System
- Tipco Tipcolene® FPT 20 FR VO PPC - UL94-V0 Flame Retardant, 20% Talc Polypropylene Copolymer
- Arlon 10842S090 Fully Cured, Unsupported Silicone Rubber
- BASF Ultramid® B3WG7 BK 00564 30% Glass Filled PA6 (Dry)
- Axiall 8424 Moldings & Extrusions Flexible PVC
Copyright © lookpolymers.com All Rights Reserved