Styron Pulse® 2000 ABS + PC
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate (PC) |
| Manufacturer | Styron |
| Trade Name | Pulse® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styron Pulse® 2000 ABS + PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | 23°C, 24hrs; ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
7.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 54.5 MPa | 7900 psi | ASTM D638 |
| Tensile Strength, Yield | 53.1 MPa | 7700 psi | ASTM D638 |
| Elongation at Break | 125 % | 125 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.28 GPa | 330 ksi | ASTM D638 |
| Flexural Strength | 84.1 MPa | 12200 psi | ASTM D790 |
| Flexural Modulus | 2.34 GPa | 340 ksi | ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | -20°F; ASTM D256 |
| 6.41 J/cm | 12.0 ft-lb/in | 73°F; ASTM D256 | |
| Dart Drop, Total Energy | 62.0 J @Temperature 22.8 °C |
45.7 ft-lb @Temperature 73.0 °F |
ASTM D3763 |
| 67.0 J @Temperature -28.9 °C |
49.4 ft-lb @Temperature -20.0 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 73.8 µm/m-°C @Temperature -40.0 - 82.2 °C |
41.0 µin/in-°F @Temperature -40.0 - 180 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 129 °C | 265 °F | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | unannealed; ASTM D648 |
| Vicat Softening Point | 143 °C | 290 °F | ASTM D1525 |
Users viewing this material also viewed the following:
- Oceanchem Group Potassium Bromate (KBrO3)
- Qualchem Danamid AFE Polyamide 66
- Materion Nibryl Beryllium Nickel Alloy (Nibryl)-360 Rod and Bar; H925 (H925) Temper; All Sizes (UNS N03360)
- Momentive Performance Materials Siloprenâ„¢ FFSL 7041 Fully Fluorinated Liquid Silicone Rubber
- Mateck Neodymium Gallate Substrate, NdGaO3
- SABIC Innovative Plastics Valox® 855 PBT (Europe-Africa-Middle East)
- A. Schulman FORMION™ FI 234 20% Mineral Reinforced Ionomer / Nylon Alloy
- Multibase Multi-Flam™ 0102 PP NH Polypropylene
- Lubrizol Advanced Materials Pearlstick® 45-40/03 Polycaprolactone based TPU (discontinued **)
Copyright © lookpolymers.com All Rights Reserved