Samyang Trirex® DMF3000S Polycarbonate, Anti-yellowing
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Optical Grade |
| Manufacturer | Samyang |
| Trade Name | Trirex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Trirex® DMF3000S Polycarbonate, Anti-yellowing.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.DMF3000S is an anti-yellowing grade.Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Water Absorption | 0.15 % | 0.15 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 20 g/10 min @Load 1.20 kg, Temperature 300 °C |
20 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 53.9 MPa | 7820 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Yield Strength | 83.4 MPa | 12100 psi | ASTM D790 |
| Flexural Modulus | 2.45 GPa | 356 ksi | ASTM D790 |
| Izod Impact, Notched | 1.96 J/cm @Thickness 3.17 mm |
3.67 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C | 33.3 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.9 | 2.9 | ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Dissipation Factor | 0.0090 | 0.0090 | ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Park Electrochemical Nelcote® E-766B Epoxy Prepreg, 285 Kevlar® Reinforced
- Albis Plastics Cellulose Acetate Propionate CP800 (Base Grade), 12% Plasticizer (discontinued **)
- Mallard Creek Polymers ROVENE® 4009 SBR Latex
- SMAC CABLE® 2524S-20-08 Damping Material
- Wingate Alloys Winco 44 Prehardened, Machinable Alloy Steel for Difficult Tooling and Maintenance Applications
- A. Schulman POLYBLAK™ 2076 Superior Black Color Concentrate, 40% Carbon Black Based In EVA
- Zircar Ceramics IB-100B Alumina Bubble
- EMS-Griltech Grilon® XA 893 Nylon 6 Monofilament (Super-Set)
- Daikin POLYFLON M-112 PTFE Molding Powder, Fine Cut
Copyright © lookpolymers.com All Rights Reserved