Styron INSPIRE™ TF7000 ES Natural Performance Polymer

Category Polymer , Thermoplastic , TPO
Manufacturer Styron
Trade Name INSPIRE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron INSPIRE™ TF7000 ES Natural Performance Polymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
INSPIRE* TF7000 ES Natural Performance Polymer DA™ is a very high stiffness (2400 MPa) TPO designed for instrument panel upper and lower components, as well as other interior trim applications where stiffness, good impact resistance, and good molded-in-color part aesthetics are important. Its high melt flow rate also allows for rapid filling of large parts in the injection molding process.Main Characteristics:Excellent surface aestheticsGood scratch & mar resistanceInstrument panel uppers/lowersInterior trim applicationsHigh flowApproved on DaimlerChrylser MS-DC265D.Information provided by DowThe Inspire brand was spun off from Dow Chemical to Styron in 2010
Physical Properties Metric English Comments
Density 1.03 g/cc
0.0372 lb/in³
ASTM D792
Melt Flow 24 g/10 min

@Load 2.16 kg,
Temperature 230 °C
24 g/10 min

@Load 4.76 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 70
70
ASTM D2240
Tensile Strength, Yield 23.0 MPa
3340 psi
ISO 527-2/50
Flexural Modulus 2.399 GPa
348.0 ksi
2.0 mm/min; ISO 178
Izod Impact, Notched (ISO) 29.0 kJ/m²
13.8 ft-lb/in²
ISO 180/1A
Dart Drop, Total Energy 23.0 J

@Temperature 23.0 °C
17.0 ft-lb

@Temperature 73.4 °F
6.6 m/sec, Ductile; ASTM D3763
29.0 J

@Temperature 0.000 °C
21.4 ft-lb

@Temperature 32.0 °F
6.6 m/sec, Ductile; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 107 °C
225 °F
Unannealed; ISO 75-2/Bf
Deflection Temperature at 1.8 MPa (264 psi) 61.1 °C
142 °F
Unannealed; ISO 75-2/Af
Flame Spread 48.0 mm/min
1.89 in/min
FMVSS302
48.0 mm/min
1.89 in/min
FMVSS302