Lucent Polymers PC/PBT-0820 Polycarbonate+PBT, Injection Grade
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Lucent Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lucent Polymers PC/PBT-0820 Polycarbonate+PBT, Injection Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Add "R" for Added ReleaseAdd "U" for UV StabilizerInformation provided by Lucent Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0090 cm/cm @Thickness 3.17 mm |
0.0090 in/in @Thickness 0.125 in |
1/8" Section |
| Melt Flow | 20 g/10 min @Load 5.00 kg, Temperature 260 °C |
20 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 62.07 MPa | 9003 psi | ASTM D638 |
| Elongation at Break | >= 80 % | >= 80 % | ASTM D638 |
| Flexural Strength | 68.97 MPa | 10000 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 3.20 J/cm @Thickness 3.17 mm |
6.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 82.22 °C | 180.0 °F | ASTM D648 |
Users viewing this material also viewed the following:
- Karina 550D35/1-AT-IS Ivory PVC Compound
- Momentive Performance Materials Silplusâ„¢ 60 EX Heat Cured Rubber - Extrusion
- Shinkong Synthetic Fibers Shinite® D201K011 PBT, Super Viscosity
- A. Schulman POLYFLAM™ E-13030B Reinforced Super Coupled Polypropylene Black
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 20 PHR N330 (HAF) Filler
- Chengdu Polyster H605 Thermoplastic Polyether-ester Elastomer (TPEE)
- Covestro Bayfol® DF-A 1-2 900296 Polycarbonate + ABS
- Axiall 50897 Moldings & Extrusions Flexible PVC
- SABIC Innovative Plastics ULTEM 1000 PEI (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved