Styron EMERGEâ„¢ 9500CR Polycarbonate (PC) / Polyethylene Terephthalate (PET)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/PET Polyester Blend , Polyester, TP , Polyethylene Terephthalate (PET)
Manufacturer Styron
Trade Name EMERGE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron EMERGEâ„¢ 9500CR Polycarbonate (PC) / Polyethylene Terephthalate (PET).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: EMERGEâ„¢ PC/PET 9500 CR advanced resin is a polycarbonate blend with excellent chemical resistance and ignition resistance properties. This grade was designed for use in medical equipment housings and other applications that are subject to repeated exposure to a variety of cleaners and disinfectants commonly used in hospitals. This grade has good aesthetics and excellent toughness. It has a UL 94 rating of V-0 at 2.0 mm. Applications:Medical device housingsInformation provided by Styron
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.0060 - 0.0095 cm/cm
0.0060 - 0.0095 in/in
ASTM D955
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ASTM D955
Melt Flow 10 g/10 min

@Load 5.00 kg,
Temperature 260 °C
 10 g/10 min

@Load 11.0 lb,
Temperature 500 °F
 ASTM D1238
13 g/10 min

@Load 5.00 kg,
Temperature 265 °C
 13 g/10 min

@Load 11.0 lb,
Temperature 509 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 110

@Thickness 3.20 mm
 110

@Thickness 0.126 in
 Injection Molded; ASTM D785
Tensile Strength at Break 45.0 MPa

@Thickness 3.20 mm
 6530 psi

@Thickness 0.126 in
 50 mm/min, Injection Molded; ASTM D638
Tensile Strength, Yield 53.0 MPa

@Thickness 3.20 mm
 7690 psi

@Thickness 0.126 in
 50 mm/min, Injection Molded; ASTM D638
Elongation at Break 150 %

@Thickness 3.20 mm
 150 %

@Thickness 0.126 in
 50 mm/min, Injection Molded; ASTM D638
Elongation at Yield 4.1 %

@Thickness 3.20 mm
 4.1 %

@Thickness 0.126 in
 50 mm/min, Injection Molded; ASTM D638
Tensile Modulus 2.33 GPa

@Thickness 3.20 mm
 338 ksi

@Thickness 0.126 in
 5 mm/min, Injection Molded; ASTM D638
Flexural Strength 82.0 MPa

@Thickness 3.20 mm
 11900 psi

@Thickness 0.126 in
 1.3 mm/min, Injection Molded; ASTM D790
Flexural Modulus 2.27 GPa

@Thickness 3.20 mm
 329 ksi

@Thickness 0.126 in
 1.3 mm/min, Injection Molded; ASTM D790
Izod Impact, Notched 7.50 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
 14.1 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
 Injection Molded; ASTM D256
Dart Drop, Total Energy 45.0 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 33.2 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 Injection Molded, Peak Energy; ASTM D3763
49.0 J

@Thickness 3.20 mm,
Temperature 0.000 °C
 36.1 ft-lb

@Thickness 0.126 in,
Temperature 32.0 °F
 Injection Molded, Peak Energy; ASTM D3763
60.0 J

@Thickness 3.20 mm,
Temperature 23.0 °C
 44.3 ft-lb

@Thickness 0.126 in,
Temperature 73.4 °F
 Injection Molded, Total Energy; ASTM D3763
62.0 J

@Thickness 3.20 mm,
Temperature 0.000 °C
 45.7 ft-lb

@Thickness 0.126 in,
Temperature 32.0 °F
 Injection Molded, Total Energy; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 74.0 µm/m-°C

@Temperature -40.0 - 80.0 °C
 41.1 µin/in-°F

@Temperature -40.0 - 176 °F
 ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 109 °C
228 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 79.0 °C
174 °F
Unannealed; ASTM D648
Vicat Softening Point 140 °C

@Load 1.02 kg
 284 °F

@Load 2.25 lb
 Rate B (120°C/h); ASTM D1525
Flammability, UL94 2.00

@Thickness 1.50 mm
 2.00

@Thickness 0.0591 in
V-0

@Thickness 2.00 mm
 V-0

@Thickness 0.0787 in
5VB

@Thickness 2.50 mm
 5VB

@Thickness 0.0984 in
Processing Properties Metric English Comments
Melt Temperature 249 - 282 °C
480 - 540 °F
Mold Temperature 43.3 - 65.6 °C
110 - 150 °F
Drying Temperature 121 °C
250 °F
Dry Time 3.00 - 4.00 hour
3.00 - 4.00 hour