- Lehmann & Voss LUVOCOM® 1106-7622 Polyether imide, with carbon fiber
Lehmann & Voss LUVOCOM® 1106-7622 Polyether imide, with carbon fiber
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) , Polyetherimide (PEI), Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1106-7622 Polyether imide, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: High-strength and high-stiff parts; low coefficient of expansion.High continuous use and heat distortion temperature. Non flammable.High dimensionally stable precision parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Bearings, sleeves, control disks, gear wheels, pump impellers, gear parts.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Water Absorption | <= 0.20 % | <= 0.20 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | |
| Melt Flow | 12.24 g/10 min @Load 5.00 kg, Temperature 360 °C |
12.24 g/10 min @Load 11.0 lb, Temperature 680 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 200 MPa | 29000 psi | |
| Elongation at Yield | 2.0 % | 2.0 % | |
| 2.7 % | 2.7 % | flexural | |
| Modulus of Elasticity | 15.0 GPa | 2180 ksi | |
| Flexural Strength | 270 MPa | 39200 psi | |
| Flexural Modulus | 12.0 GPa | 1740 ksi | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | edgewise; ISO 179 1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 170 °C | 338 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | |
| Flammability, UL94 | V-0 | V-0 | not recognized by UL |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 1.00e+6 ohm | <= 1.00e+6 ohm | |
| Insulation Resistance | 1000 - 1.00e+6 ohm | 1000 - 1.00e+6 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 380 °C | 716 °F | mass temp |
| Nozzle Temperature | 350 - 400 °C | 662 - 752 °F | |
| Zone 1 | 330 - 350 °C | 626 - 662 °F | |
| Zone 2 | 340 - 390 °C | 644 - 734 °F | |
| Zone 3 | 350 - 400 °C | 662 - 752 °F | |
| Mold Temperature | 150 - 180 °C | 302 - 356 °F | |
| Drying Temperature | 120 °C @Time >=28800 sec |
248 °F @Time >=8.00 hour |
Dehumidifying dryer |
| 150 °C @Time >=14400 sec |
302 °F @Time >=4.00 hour |
or |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Nanocyl PLASTICYL™ PP2001 Polypropylene with 3.2 wt% Multi-Wall Carbon Nanotubes
- Lucite International Elvacite ® 3000 Acrylic Resin
- Solvay Specialty Polymers Cogegum® AFR/920-UV Polyolefin
- Chase Plastics CP Pryme® NN100L (COND, 50% RH) Nylon 66, Internally Lubricated
- Zircar Refractory Composites ZIRCAL-45 Refractory Board
- Eagle Brass 220 Commercial Bronze, 1/2 Hard
- Eastman Tenite Butyrate 285A3720010 Clear, Trsp Cellulose Acetate Butyrate
- 3M Hi-Strength 94 ET Cylinder Spray Adhesive
- Lanxess Durethan® BC 700 HTS 900116 Nylon 6/66 (discontinued **)
Copyright © lookpolymers.com All Rights Reserved