Samsung Cheil Industries StarexÂ® LX-0970 MS ABS, Unreinforced Metallic-Look

Category	Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded
Manufacturer	Samsung, Cheil Industries
Trade Name	Starex®
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Samsung Cheil Industries StarexÂ® LX-0970 MS ABS, Unreinforced Metallic-Look.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Luminous Grade - gives aesthetics of a painted surface without painting. Reduces time, cost, and environmental hazards (such as soilvents).Information provided by Samsung Cheil Industries.

Physical Properties	Metric	English	Comments
Specific Gravity	1.05 g/cc	1.05 g/cc	ASTM D792
Melt Flow	20 g/10 min @Load 10.0 kg, Temperature 220 Â°C	20 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	108	108	ASTM D785
Tensile Strength at Break	33.3 MPa	4830 psi	5 mm/min; ASTM D638
Tensile Strength, Yield	43.1 MPa	6260 psi	50 mm/min; ASTM D638
Elongation at Break	16 %	16 %	5 mm/min; ASTM D638
Tensile Modulus	2.26 GPa	327 ksi	5 mm/min; ASTM D638
Flexural Strength	68.6 MPa	9950 psi	2.8 mm/min; ASTM D790
Flexural Modulus	2.26 GPa	327 ksi	2.8 mm/min; ASTM D790
Izod Impact, Notched	1.57 J/cm @Thickness 6.35 mm	2.94 ft-lb/in @Thickness 0.250 in	ASTM D256
	1.67 J/cm @Thickness 3.17 mm	3.12 ft-lb/in @Thickness 0.125 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	95.0 Â°C @Thickness 6.40 mm	203 Â°F @Thickness 0.252 in	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	89.0 Â°C @Thickness 6.40 mm	192 Â°F @Thickness 0.252 in	ASTM D648
Vicat Softening Point	98.0 Â°C	208 Â°F	B/50; ISO R306
	99.0 Â°C	210 Â°F	B/120; ISO R306