Styron EMERGEâ„¢ 8600-20 Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer Styron
Trade Name EMERGE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron EMERGEâ„¢ 8600-20 Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
EMERGEâ„¢ PC 8600-20 is a translucent, ignition-resistant and easy flow polycarbonate resin. The resin contains no bromine, chlorine or phosphate additives and is intended to comply with global environmental standards. It has a UL94 flammability rating of V-0 at 1.5 mm.Applications: A broad range of injection molded applications in teh electronics, electrical adn iformation technology equipment markets.Information provided by DowThis product line was spun off from Dow Chemical to Styron in 2010.
Physical Properties Metric English Comments
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183B
Linear Mold Shrinkage 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
ISO 294-4
Melt Flow 20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
 20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Rockwell R 123
123
ISO 2039/2
Tensile Strength at Break 58.0 MPa

@Thickness 4.00 mm
 8410 psi

@Thickness 0.157 in
 50mm/min, injection molded, unannealed; ISO 527-2
Tensile Strength, Yield 60.0 MPa

@Thickness 4.00 mm
 8700 psi

@Thickness 0.157 in
 50mm/min, injection molded, unannealed; ISO 527-2
Elongation at Break 100 %

@Thickness 4.00 mm
 100 %

@Thickness 0.157 in
 50mm/min, injection molded, unannealed; ISO 527-2
Elongation at Yield 6.0 %

@Thickness 4.00 mm
 6.0 %

@Thickness 0.157 in
 50mm/min, injection molded, unannealed; ISO 527-2
Flexural Strength 94.0 MPa

@Thickness 4.00 mm
 13600 psi

@Thickness 0.157 in
 2mm/min, injection molded, unannealed; ISO 178
Flexural Modulus 2.40 GPa

@Thickness 4.00 mm
 348 ksi

@Thickness 0.157 in
 2mm/min, injection molded, unannealed; ISO 178
Izod Impact, Notched (ISO) 50.0 kJ/m²

@Thickness 4.00 mm
 23.8 ft-lb/in²

@Thickness 0.157 in
 ISO 180/A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 0.650 µm/m-°C
0.361 µin/in-°F
ASTM D696
Hot Ball Pressure Test >= 125 °C
>= 257 °F
IEC 60335-1
Deflection Temperature at 0.46 MPa (66 psi) 136 °C
277 °F
unannealed; ISO 75-B
Deflection Temperature at 1.8 MPa (264 psi) 122 °C
252 °F
unannealed; ISO 75-A
Vicat Softening Point 143 °C
289 °F
50°C / 50N; ISO 306-B50
150 °C
302 °F
120°C / 10N; ISO 306-A120
UL RTI, Electrical 125 °C
257 °F
UL 746
UL RTI, Mechanical with Impact 125 °C
257 °F
UL 746
UL RTI, Mechanical without Impact 125 °C
257 °F
UL 746
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
Oxygen Index 35 %
35 %
ISO 4589-2
Glow Wire Test 960 °C

@Thickness 1.00 mm
 1760 °F

@Thickness 0.0394 in
 IEC 60695-2-10
Processing Properties Metric English Comments
Melt Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 70.0 - 100 °C
158 - 212 °F
Drying Temperature 125 °C
257 °F
Dry Time 3 - 4 hour
3 - 4 hour