SABIC Innovative Plastics LNP LUBRICOMP UCL36ASP PPA (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polyphthalamide (PPA)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP UCL36ASP PPA (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* LUBRICOMP* UCL36ASP is a compound based on Polyphthalamide resin containing Carbon Fiber, PTFE. Added features include; Internally Lubricated, Electrically Conductive, Heat Stabilized.

Physical Properties	Metric	English	Comments
Density	1.42 g/cc	0.0513 lb/inÂ³	ISO 1183
Water Absorption	0.40 % @Time 86400 sec	0.40 % @Time 24.0 hour	ISO 62-1
Linear Mold Shrinkage, Flow	0.00050 - 0.0015 cm/cm	0.00050 - 0.0015 in/in	SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	256 MPa	37100 psi	5 mm/min; ISO 527
Elongation at Break	1.3 %	1.3 %	5 mm/min; ISO 527
Tensile Modulus	25.1 GPa	3640 ksi	1 mm/min; ISO 527
Flexural Yield Strength	340 MPa	49300 psi	2 mm/min; ISO 178
Flexural Modulus	19.9 GPa	2890 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	7.00 kJ/mÂ²	3.33 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	40.0 kJ/mÂ²	19.0 ft-lb/inÂ²	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	8.00 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	4.44 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	51.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	28.3 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi)	270 Â°C	518 Â°F	Flatw 80104 sp=64mm; ISO 75/Af

Electrical Properties	Metric	English	Comments
Surface Resistance	10 - 1000 ohm	10 - 1000 ohm	ASTM D257