Styron CALIBREâ„¢ 2060-6 Polycarbonate Resin

Category	Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer	Styron
Trade Name	CALIBRE™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Styron CALIBREâ„¢ 2060-6 Polycarbonate Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Overview: CALIBREâ„¢ 2060-6 polycarbonate resin is used in medical applications involving steam or ethylene oxide sterilization â€“ through suitability for use in these applications is dependent upon autoclave cycle times and temperatures. CALIBRE 2060-6 provides exceptional clarity, heat resistance, impact strength, and processability, and has low contamination levels. The CALIBRE 2000 series of resins have been evaluated by certain biocompatibility tests based on ISO 10993-1 (Biological Evaluation of Medical Devices) and are suitable for use in approved medical applications.Applications:Medical applicationsInformation provided by Styron

Physical Properties	Metric	English	Comments
Density	1.20 g/cc	0.0434 lb/inÂ³	ISO 1183/A; ASTM D792
Water Absorption	0.32 % @Temperature 23.0 Â°C	0.32 % @Temperature 73.4 Â°F	Equilibrium, 50% RH; ISO 62; ASTM D570
	0.15 % @Temperature 23.0 Â°C, Time 86400 sec	0.15 % @Temperature 73.4 Â°F, Time 24.0 hour	ISO 62; ASTM D570
Linear Mold Shrinkage, Flow	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	ISO 294-4; ASTM D955
Melt Flow	6.0 g/10 min @Load 1.20 kg, Temperature 300 Â°C	6.0 g/10 min @Load 2.65 lb, Temperature 572 Â°F	ISO 1133; ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	73	73	ASTM D785
Hardness, Rockwell R	118	118	ASTM D785
Tensile Strength at Break	72.0 MPa	10400 psi	ISO 527-2/50
	72.4 MPa	10500 psi	50 mm/min; ASTM D638
Tensile Strength, Yield	60.0 MPa	8700 psi	50 mm/min; ASTM D638; ISO 527-2/50
Elongation at Break	150 %	150 %	50 mm/min; ASTM D638; ISO 527-2/50
Tensile Modulus	2.41 GPa	350 ksi	50 mm/min; ASTM D638; ISO 527-2/50
Flexural Strength	96.0 MPa	13900 psi	2.0 mm/min; ISO 178
	96.5 MPa	14000 psi	Method I (3 point load), 2.0 mm/min; ASTM D790
Flexural Modulus	2.41 GPa	350 ksi	Method I (3 point load), 2.0 mm/min; ASTM D790; ISO 178
Izod Impact, Notched	9.10 J/cm @Temperature 23.0 Â°C	17.0 ft-lb/in @Temperature 73.4 Â°F	ASTM D256
Izod Impact, Notched (ISO)	88.0 kJ/mÂ² @Temperature 23.0 Â°C	41.9 ft-lb/inÂ² @Temperature 73.4 Â°F	ISO 180/A
Izod Impact, Unnotched (ISO)	NB @Temperature 23.0 Â°C	NB @Temperature 73.4 Â°F	ISO 180; ASTM D256A
Tensile Impact Strength	588 kJ/mÂ²	280 ft-lb/inÂ²	ASTM D1822
Dart Drop, Total Energy	90.4 J	66.7 ft-lb	3.39 m/sec; ASTM D3763
Abrasion	45	45	[%] Taber; ASTM D1004