Kotec Carbotex K-40UV Polycarbonate, General Purpose, UV Stability Grade
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, UV Stabilized |
| Manufacturer | Kotec Corp |
| Trade Name | Carbotex |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kotec Carbotex K-40UV Polycarbonate, General Purpose, UV Stability Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: UV stability, Medium viscosity, TransparentApplications: OA equipment, Communications, Precision parts, Machineries, Lighting fixtures, Safety products, E & E parts, Household applications, Leisure articlesInformation provided by Kotec Corporation
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 0.20 % @Temperature 23.0 °C, Time 86400 sec |
0.20 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D995 |
| Melt Flow | 12 g/10 min @Load 1.20 kg, Temperature 300 °C |
12 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | |
| Tensile Strength at Break | 63.0 MPa | 9140 psi | ASTM D638 |
| Elongation at Break | 120 % | 120 % | ASTM D638 |
| Flexural Strength | 85.0 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 2.16 GPa | 313 ksi | ASTM D790 |
| Izod Impact, Notched | 8.30 J/cm @Temperature 23.0 °C |
15.5 ft-lb/in @Temperature 73.4 °F |
V-Notched 1/8"; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat Distortion Temperature | 133 °C | 271 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.58 | 1.58 | ASTM D542 |
| Haze | <= 1.0 % @Thickness 3.00 mm |
<= 1.0 % @Thickness 0.118 in |
ASTM D1003 |
| Transmission, Visible | 89 % @Thickness 3.00 mm |
89 % @Thickness 0.118 in |
ASTM D1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
| Dissipation Factor | 0.0090 @Frequency 1.00e+6 Hz |
0.0090 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 110 sec | 110 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Nye Lubricants 740S (RL) Synthetic Oil
- Epoxy Novolac 27%, Carbon fabric 73%
- LyondellBasell Alathon® H6017 High Density Polyethylene, Injection Molding Grade
- LG Chemical Lupox® GP2100 PBT+GF10%
- Von Roll Isola IMI Varnish 73522 Solventless Polyester Varnish for Electrical Insulation
- A. Schulman POLYBATCH™ Blue 4500 Concentrate Based In Polyethylene
- BASF Heligoen® Blue L 6901 F Color Additive
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 0.5 PHR Sulfur
- Trelleborg Fillite® PG (300LF) Alumino-silicate Cenospheres
- E-Polymers SEPAZ® C130HS 30% Glass Fiber Reinforced High Temperature Stabilized LCP Resin
Copyright © lookpolymers.com All Rights Reserved