Industrial Laminates/Norplex NP664 Paper Base Laminate

Category Polymer , Thermoset
Manufacturer Industrial Laminates/Norplex
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Industrial Laminates/Norplex NP664 Paper Base Laminate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Low cost room temperature punching grade with mechanical and electrical properties similar to NP612. This version is made with pigment cover plies on the surface.Thickness Tested: 0.062", 0.125" & 0.500"
Physical Properties Metric English Comments
Specific Gravity 1.30 - 1.40 g/cc

@Thickness 1.57 mm
 1.30 - 1.40 g/cc

@Thickness 0.0620 in
 ASTM D792
Moisture Absorption at Equilibrium 5.5 %

@Thickness 1.57 mm
 5.5 %

@Thickness 0.0620 in
 ASTM D229
Mechanical Properties Metric English Comments
Hardness, Rockwell M 80 - 100

@Thickness 1.57 mm
 80 - 100

@Thickness 0.0620 in
 ASTM D785
Tensile Strength, Yield 86.2 MPa

@Thickness 1.57 mm
 12500 psi

@Thickness 0.0620 in
 CW; ASTM D638
155 MPa

@Thickness 1.57 mm
 22500 psi

@Thickness 0.0620 in
 LW; ASTM D638
Modulus of Elasticity 6.89 GPa

@Thickness 1.57 mm
 1000 ksi

@Thickness 0.0620 in
 CW; ASTM D229
8.27 GPa

@Thickness 1.57 mm
 1200 ksi

@Thickness 0.0620 in
 LW; ASTM D229
Flexural Strength 165 MPa

@Thickness 1.57 mm
 24000 psi

@Thickness 0.0620 in
 CW; ASTM D790
179 MPa

@Thickness 1.57 mm
 26000 psi

@Thickness 0.0620 in
 LW; ASTM D790
Compressive Strength 207 MPa

@Thickness 12.7 mm
 30000 psi

@Thickness 0.500 in
 ASTM D695
Shear Strength 75.8 MPa

@Thickness 15.7 mm
 11000 psi

@Thickness 0.620 in
 ASTM D732
Izod Impact, Unnotched 0.331 J/cm

@Thickness 12.7 mm
 0.620 ft-lb/in

@Thickness 0.500 in
 CW, Cond E-48/50; ASTM D256
0.358 J/cm

@Thickness 12.7 mm
 0.670 ft-lb/in

@Thickness 0.500 in
 LW, Cond E-48/50; ASTM D256
Thermal Properties Metric English Comments
CTE, linear 20.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 11.1 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
CTE, linear, Transverse to Flow 18.0 µm/m-°C

@Thickness 1.57 mm,
Temperature 20.0 °C
 10.0 µin/in-°F

@Thickness 0.0620 in,
Temperature 68.0 °F
 x-axis; IPC-TM 650-2.4.24
Maximum Service Temperature, Air 130 °C
266 °F
Flammability, UL94 HB

@Thickness 1.57 mm
 HB

@Thickness 0.0620 in
Electrical Properties Metric English Comments
Dielectric Strength 11.8 kV/mm

@Thickness 1.57 mm
 300 kV/in

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S.T.
19.7 kV/mm

@Thickness 1.57 mm
 500 kV/in

@Thickness 0.0620 in
 Cond A; ASTM D229 S.T.
Dielectric Breakdown 10000 V

@Thickness 1.57 mm
 10000 V

@Thickness 0.0620 in
 Cond D-48/50; ASTM D229 S/S
60000 V

@Thickness 1.57 mm
 60000 V

@Thickness 0.0620 in
 Cond A; ASTM D229 S/S
Arc Resistance 110 sec

@Thickness 3.17 mm
 110 sec

@Thickness 0.125 in
 ASTM D495
Comparative Tracking Index 180 V

@Thickness 3.17 mm
 180 V

@Thickness 0.125 in
 ASTM D3638
Descriptive Properties Value Comments
Bond Strength 1100 lb
0.5", ASTM D229
Color Natural, Black