Material Notes:

Terluran HH-106 is an injection molding ABS grade with high resistance to heat deformation and impact.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.

Physical Properties	Metric	English	Comments
Density	1.05 g/cc	0.0379 lb/inÂ³	ISO 1183
Linear Mold Shrinkage	0.0055 cm/cm	0.0055 in/in	ASTM Data; MD
Melt Flow	7.0 g/10 min @Load 10.0 kg, Temperature 220 Â°C	7.0 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ISO 1133
	7.0 g/10 min @Load 10.0 kg, Temperature 220 Â°C	7.0 g/10 min @Load 22.0 lb, Temperature 428 Â°F	ASTM Test

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	51.0 MPa	7400 psi	50mm/min; ISO 527
	52.0 MPa	7540 psi	2 in/min; ASTM Test
Elongation at Break	9.0 %	9.0 %	50mm/min, Nominal strain; ISO 527
Elongation at Yield	3.0 %	3.0 %	50mm/min; ISO 527
	3.0 %	3.0 %	2 in/min; ASTM Test
Tensile Modulus	2.40 GPa	348 ksi	1mm/min; ISO 527
	2.50 GPa	363 ksi	ASTM Test
Flexural Strength	72.0 MPa	10400 psi	ISO Data
	77.0 MPa	11200 psi	ASTM Test
Flexural Modulus	2.40 GPa	348 ksi	ASTM Test
Izod Impact, Notched	0.750 J/cm @Temperature -30.0 Â°C	1.41 ft-lb/in @Temperature -22.0 Â°F	ASTM Test
	2.30 J/cm @Thickness 3.17 mm	4.31 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	19.0 kJ/mÂ²	9.04 ft-lb/inÂ²	ISO Test
Charpy Impact Unnotched	19.0 J/cmÂ²	90.4 ft-lb/inÂ²	ISO 179
	10.0 J/cmÂ² @Temperature -30.0 Â°C	47.6 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179
Charpy Impact, Notched	1.70 J/cmÂ²	8.09 ft-lb/inÂ²	ISO 179
	0.700 J/cmÂ² @Temperature -30.0 Â°C	3.33 ft-lb/inÂ² @Temperature -22.0 Â°F	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	95.0 Âµm/m-Â°C	52.8 Âµin/in-Â°F	ISO 11359
Deflection Temperature at 0.46 MPa (66 psi)	111 Â°C	232 Â°F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	106 Â°C	223 Â°F	ISO 75
Vicat Softening Point	106 Â°C	223 Â°F	Rate "A" Loading 2 (50 degC/h 50N); ASTM Test
	106 Â°C	223 Â°F	(50 Â°C/h / 50N) - B/50; ISO 306
Flammability, UL94	HB @Thickness 1.50 mm	HB @Thickness 0.0591 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+13 ohm-cm	>= 1.00e+13 ohm-cm	IEC 60093
Dielectric Strength	39.0 kV/mm	991 kV/in	IEC 60243-1

Processing Properties	Metric	English	Comments
Melt Temperature	250 Â°C	482 Â°F	Injection molding
Mold Temperature	105 Â°C	221 Â°F	Ejection temperature
Injection Velocity	60.0 mm/sec	2.36 in/sec	Injection molding

Descriptive Properties	Value	Comments
Color	Natural
Commercial Status	North America and Europe
Form	Pellets
Impact Modified	Yes
NSF Std. 51	No
NSF Std. 61	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
Special characteristic	Heat stabilized or stable to heat
	Platable
UL.UL-C	Yes
USP Class VI	No