Eurostar Star L PA66 15Y D61 PA66, Carbon Filled, Injection Molded
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Carbon Fiber Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Star L |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Star L PA66 15Y D61 PA66, Carbon Filled, Injection Molded.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Star L PA66 15Y D61 is a PTFE/Silicone Oil Lubricated, Carbon Fiber Reinforced, Polyamide 66 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Thickness 4.00 mm |
0.0020 - 0.0040 in/in @Thickness 0.157 in |
E2P method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 170 MPa | 24700 psi | ISO 527 |
| Elongation at Break | 2.3 % | 2.3 % | ISO 527 |
| Flexural Strength | 221 MPa | 32100 psi | ISO 178 |
| Flexural Modulus | 9.30 GPa | 1350 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.40 kJ/m² | 2.57 ft-lb/in² | 80x10x4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 42.0 kJ/m² | 20.0 ft-lb/in² | 80x10x4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 265 °C | 509 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80x10x4, sp=64 mm; ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 265 - 275 °C | 509 - 527 °F | |
| Zone 2 | 270 - 280 °C | 518 - 536 °F | |
| Zone 3 | 270 - 280 °C | 518 - 536 °F | |
| Melt Temperature | 270 - 280 °C | 518 - 536 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.15 - 0.25 % | 0.15 - 0.25 % |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 6/66 FRc 3 TS PA6/66, flame retardant
- Lubriplate Food Grade Silicone Lubricant Food Grade Spray Lubricant
- Solvay Chemicals NOCOLOK® Li Flux
- Sibur SKI-3 Superior Quality, 2nd Group Isoprene Rubber (IR)
- Silberline Sparkle Silver® 3166-AR
- SABIC Innovative Plastics Xenoy® XD549S PBT+PC (Europe-Africa-Middle East)
- Borealis Xmod™ MC55 High Crystalline Polypropylene Copolymer
- Dow TUFLIN™ HS-7066 NT 7 Linear Low Density Polyethylene Resin
- Lubrizol Estane® GP 52 DT Thermoplastic Polyurethane
Copyright © lookpolymers.com All Rights Reserved