Styrolution Terblend® N NG-06 30% Glass Filled ABS/PA6 (Dry)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend, Glass Reinforced , Nylon |
| Manufacturer | Styrolution |
| Trade Name | Terblend® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution Terblend® N NG-06 30% Glass Filled ABS/PA6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Terblend N NG-06 is a 30% glass fiber reinforced ABS/PA6 blend with extra high rigidity and dimensional stability.Information provided by STYROLUTION, which is a joint venture between BASF and INEOS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Water Absorption | 3.4 % | 3.4 % | ISO 62 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | 23°C/50% R.H.; ISO 62 |
| Melt Flow | 6.0 g/10 min @Load 10.0 kg, Temperature 240 °C |
6.0 g/10 min @Load 22.0 lb, Temperature 464 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 105 MPa | 15200 psi | 5mm/min; ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 |
| Tensile Modulus | 7.50 GPa | 1090 ksi | 1mm/min; ISO 527 |
| Flexural Strength | 130 MPa | 18900 psi | ISO Data |
| Flexural Modulus | 6.50 GPa | 943 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO Test |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179 |
| 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | ISO 179 |
| 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 188 °C | 370 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 107 °C | 225 °F | ISO 75 |
| Vicat Softening Point | 120 °C | 248 °F | (50 °C/h / 50N) - B/50; ISO 306 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 2.9 @Frequency 1.00e+6 Hz |
2.9 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dissipation Factor | 0.013 @Frequency 1.00e+6 Hz |
0.013 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 265 °C | 509 °F | Injection molding |
| Injection Velocity | 65.0 mm/sec | 2.56 in/sec | Injection molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Commercial Status | Active America | |
| Primary Processing Technique | Injection Molding | |
| UL.UL-C | Yes |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPE A 7301 BLK
- Nitriflex N-6420 NBR / PVC
- LyondellBasell Pro-faxâ„¢ SR257M Polypropylene Copolymer
- Kennametal Stellite Stellite® 107 Cobalt Alloy
- Grupo Repol Dinalon® B1S25 G25XV0 PA6 25% Glass Fiber V0
- Samsung Cheil Industries Infino® HI-1001BP PC/ABS, Metal Plating Grade
- DSM Akulon® K224-G0 Nylon 6-50% Glass Reinforced (European Grade) (Dry)
- Aclo Accutech Polypropylene Copolymer CP0437W40L Wollastonite Reinforced
- BASF Ultramid® HMG13 HS BK-102 63% Glass Filled PA6 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved