Styrolution PS 153F GPPS
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Heat Resistant Grade |
| Manufacturer | Styrolution |
| Trade Name | PS |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution PS 153F GPPS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Styrolution PS 153F is general purpose polystyrene with high heat resistance and good flow properties. Styrolution PS 153F is free of internal lubricants, e.g. zinc stearate.Free of internal lubricantsGood flow characteristicsInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
50% RH; ISO 62 |
| Water Absorption at Saturation | <= 0.10 % @Temperature 23.0 °C |
<= 0.10 % @Temperature 73.4 °F |
ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ISO 294-4 |
| Melt Flow | 7.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
7.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 150 MPa | 21800 psi | ISO 2039-1 |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | ISO 527 |
| Elongation at Yield | 1.5 % | 1.5 % | ISO 527 |
| Tensile Modulus | 3.05 GPa | 442 ksi | ISO 527 |
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 |
| Charpy Impact Unnotched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.160 W/m-K | 1.11 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ISO 75 |
| Vicat Softening Point | 101 °C @Load 5.10 kg |
214 °F @Load 11.2 lb |
120°C/h; ASTM D 1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+18 ohm-cm | >= 1.00e+18 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 - 280 °C | 356 - 536 °F | ISO 294 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP FARADEX MS003 PP (Europe-Africa-Middle East)
- Michelman® ThermaGloss® 420 Water based over print varnish
- Heatbath/Park Carbo Fluid H Carburizer
- Teknor Apex Elexar® EL-8421 Thermoplastic Elastomer
- Total PPC 4820WZ Polypropylene, Impact Copolymer
- ChevronTexaco Polystar® Synthetic 4602 NLGI Grade
- Dow DNDA-8320 NT 7 Linear Low Density Polyethylene Resin
- Fainplast Compounds MPH 62/D Medical Flexible PVC, Extrusion
- Haynes Hastelloy® B-3® alloy, after elevated temperature exposure
- DSM Akulon® F132-E Nylon 6 (European Grade) (Dry) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved