Styrolution NOVODUR® P2MC ABS, Injection Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Molded , Acrylonitrile Butadiene Styrene (ABS), Plating Grade |
| Manufacturer | Styrolution |
| Trade Name | Novodur® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Styrolution NOVODUR® P2MC ABS, Injection Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection molding grade for plating; very good ratio between toughness, heat resistance and flow.Applications: All parts to plating: e.g. sanitary parts.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | |
| Water Absorption | 0.30 % | 0.30 % | Saturation in water |
| Water Absorption at Saturation | 0.30 % | 0.30 % | |
| Melt Flow | 25 g/10 min @Load 10.0 kg, Temperature 220 °C |
25 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | |
| Elongation at Yield | 2.4 % | 2.4 % | |
| Tensile Modulus | 2.20 GPa | 319 ksi | |
| Charpy Impact Unnotched | NB | NB | |
| 1.00 J/cm² @Temperature -30.0 °C |
4.76 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 2.40 J/cm² | 11.4 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C |
55.6 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 96.0 °C | 205 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 92.0 °C | 198 °F | |
| Vicat Softening Point | 95.0 °C | 203 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | |
| Dielectric Constant | 2.7 @Frequency 1e+6 Hz |
2.7 @Frequency 1e+6 Hz |
|
| 2.8 @Frequency 100 Hz |
2.8 @Frequency 100 Hz |
||
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | |
| Dissipation Factor | 0.0050 @Frequency 100 Hz |
0.0050 @Frequency 100 Hz |
|
| 0.0070 @Frequency 1e+6 Hz |
0.0070 @Frequency 1e+6 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
Users viewing this material also viewed the following:
- PolyOne Dynaflex™ G7930-9001-02 Thermoplastic Elastomer (TPE)
- Albis Plastics ASA 02A 811 Unreinforced (discontinued **)
- Hexcel® HexWeb® CR-PAA™ 3/8-5052-0.001 Phosphoric Acid Anodized Aluminum Honeycomb
- Dow Corning SYL-OFF® PMCPEM 7974 Emulsion Coating
- Epoxy Technology EPO-TEK® OG178 UV Cure Optical Epoxy
- Eurostar Staramide RB008 PA66, 40% Glass Bead Filled, Injection Molded
- Ceradyne Ceralloy® 147-A Hot Pressed Silicon Nitride (Si3N4)
- Lubrizol ESTANE® 54630 Ether Based Thermoplastic Polyurethane (European Grade)
- HP Alloys HPA COBALT Alloy 6BH, Wear Resistant, (Co-Cr-W) (UNS R30016)
Copyright © lookpolymers.com All Rights Reserved