Stellarchem SV-B87E TPV Compound
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV) |
| Manufacturer | Stellarchem |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Stellarchem SV-B87E TPV Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This grade of Stellarchem SV series is a dynamic crosslinked, EPDM/PP compound. It's design to replace thermoset elastomers, such as EPDM, and traditional Thermoplastic TPVs. It can be process on conventional thermoplastics equipment for injection, extrusion or blow molding, provide the performance of vulcanized rubber with the advantage of low cost thermoplastic processing. It's a soft, EPDM/PP based, completely recyclable & colorable elastomer material. It's formulated to overmold to PP thermoplastics in normal dual injection & extrusion processing.Information provided by Stellarchem Polymer & Industrial
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ASTM D792 |
| Particle Mesh Size | 80 - 150 Mesh | 80 - 150 Mesh | |
| Melt Flow | 85 g/10 min @Load 10.0 kg, Temperature 230 °C |
85 g/10 min @Load 22.0 lb, Temperature 446 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 94 | 94 | ASTM D2240 |
| Tensile Strength, Ultimate | 13.7 MPa | 1990 psi | ASTM D412 |
| Elongation at Break | 680 % | 680 % | ASTM D412 |
| 100% Modulus | 0.07056 GPa | 10.23 ksi | ASTM D412 |
| Tear Strength | 76.5 kN/m | 437 pli | ASTM D412 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 160 - 170 °C | 320 - 338 °F | Metering Temperature, Extrusion |
| Rear Barrel Temperature | 150 - 160 °C | 302 - 320 °F | Extrusion |
| 160 - 190 °C | 320 - 374 °F | Injection Molding | |
| Middle Barrel Temperature | 155 - 165 °C | 311 - 329 °F | Transition, Extrusion |
| 170 - 190 °C | 338 - 374 °F | Injection Molding | |
| Front Barrel Temperature | 170 - 180 °C | 338 - 356 °F | Extrusion |
| 180 - 200 °C | 356 - 392 °F | Injection Molding | |
| Nozzle Temperature | 190 - 210 °C | 374 - 410 °F | Injection Molding |
| Die Temperature | 170 - 180 °C | 338 - 356 °F | Extrusion |
| Melt Temperature | 150 - 180 °C | 302 - 356 °F | Extrusion |
| 160 - 200 °C | 320 - 392 °F | Injection Molding | |
| Mold Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Injection Molding |
| Injection Pressure | 5.00 - 40.0 MPa | 725 - 5800 psi | Injection Molding |
| Back Pressure | 0.500 - 1.00 MPa | 72.5 - 145 psi | Injection Molding |
| Screw Speed | 60 - 100 rpm | 60 - 100 rpm | Extrusion |
| 100 - 200 rpm | 100 - 200 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Polimeri Europa Flexirene® FG 30 U Butene Copolymer Linear Low Density Polyethylene
- REXtac Rextac® RT 1230 Amorphous Polyalphaolefin (APAO)
- Ineos Nova Zyntar® F7080UV Developmental Flame Retardant Polystyrene (discontinued **)
- DuPont Elvax® 3174SHB Ethylene-Vinyl Acetate Copolymer Resin for Coextrusion, Cast Film (discontinued **)
- Epichlorohydrin Rubber (CO, ECO)
- LyondellBasell Petrothene® NA831000 Low Density Polyethylene
- SABIC Innovative Plastics LNP THERMOCOMP DX06313I PC (Asia Pacific)
- A. Schulman POLYBATCH™ Green 3315 Concentrate Based In Polyethylene
- Buckeye Polymers BP ABS 3726 E ABS
- DuPont Performance Polymers Neoprene SW Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved