Stellarchem AB835EM TPE Compound
| Category | Polymer , Thermoplastic , Elastomer, TPE , Olefinic TPE |
| Manufacturer | Stellarchem |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Stellarchem AB835EM TPE Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This grade of Stellarchem TPE is shear dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It's a soft, elastomeric polyolefin based, completely recyclable, colorable & non-hygroscopic thermoplastics elastomer material.Information provided by Stellarchem Polymer & Industrial
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | |
| Particle Mesh Size | 80 - 150 Mesh | 80 - 150 Mesh | |
| Melt Flow | 12.66 g/10 min | 12.66 g/10 min | JIS K7210 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 38 | 38 | JIS K6301 |
| Tensile Strength, Ultimate | 1.08 MPa | 156 psi | JIS K6301 |
| Elongation at Break | 547 % | 547 % | JIS K6301 |
| 100% Modulus | 0.000686 GPa | 0.0995 ksi | JIS K6301 |
| 300% Modulus | 0.000588 GPa | 0.0853 ksi | JIS K6301 |
| Tear Strength | 9.51 kN/m | 54.3 pli | JIS K6301-B |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 - 220 °C | 392 - 428 °F | Metering Temperature, Extrusion |
| Rear Barrel Temperature | 160 - 180 °C | 320 - 356 °F | Injection Molding |
| 160 - 180 °C | 320 - 356 °F | Extrusion | |
| Middle Barrel Temperature | 180 - 200 °C | 356 - 392 °F | Injection Molding |
| 180 - 200 °C | 356 - 392 °F | Transition, Extrusion | |
| Front Barrel Temperature | 200 - 220 °C | 392 - 428 °F | Injection Molding |
| 220 - 230 °C | 428 - 446 °F | Extrusion | |
| Nozzle Temperature | 220 - 230 °C | 428 - 446 °F | Injection Molding |
| Die Temperature | 195 - 210 °C | 383 - 410 °F | Extrusion |
| Melt Temperature | 180 - 230 °C | 356 - 446 °F | Injection Molding |
| 180 - 230 °C | 356 - 446 °F | Extrusion | |
| Mold Temperature | 25.0 - 40.0 °C | 77.0 - 104 °F | Injection Molding |
| Injection Pressure | 5.00 - 40.0 MPa | 725 - 5800 psi | Injection Molding |
| Back Pressure | 0.500 - 1.00 MPa | 72.5 - 145 psi | Injection Molding |
| Screw Speed | 60 - 100 rpm | 60 - 100 rpm | Extrusion |
| 100 - 200 rpm | 100 - 200 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Multibase SILASTIC® C7-4565 CADOX BSD Dow-Corning Biomedical Grade ETR Elastomer
- LNP NORYL® EXCP0112 PPS + Polyphenylene Ether, 40% Glass / Mineral Reinforcement (discontinued **)
- ICO Polymers ICORENEâ„¢ 324-3561 LMDPE Rotational Molding Resin
- LG Chemical LUPOL TE-5202U Thermoplastic Elastomer Alloy, 20% Polymer Alloy, High Impact, High Modulus
- Special Metals INCONEL® C276 Nickel Superalloy Bar
- UBE UBESTA® 3030U Nylon 12 (After Acetic Acid (10%) for 1000 hours)
- CP-Polymer-Technik Wellamid® 6000 GVS 10/20 HWCP 10% Glass Fiber and 20% Glass Sphere Nylon 6, Heat Stabilized, Conditioned
- BASF Heligoen® Blue L 7081 D Color Additive
- Alliance Polymers Zythane™ 3045D Thermoplastic Polyurethane Elastomer
- Aremco Aremco-Bond™ 2318 High Performance Epoxide
Copyright © lookpolymers.com All Rights Reserved