- Star Plastics PCGF10 Molding Grade PC with 10% Glass
Star Plastics PCGF10 Molding Grade PC with 10% Glass
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 10% Glass Filled |
| Manufacturer | Star Plastics, Inc |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Star Plastics PCGF10 Molding Grade PC with 10% Glass.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Star Plastics, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 15 g/10 min @Load 1.20 kg, Temperature 300 °C |
15 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 65.5 MPa | 9500 psi | ASTM D638 |
| Tensile Modulus | 3.10 GPa | 450 ksi | ASTM D638 |
| Flexural Yield Strength | 100 MPa | 14500 psi | ASTM D790 |
| Flexural Modulus | 3.10 GPa | 450 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | 73°F, 0.125 in.; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | unannealed, .125in; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 288 - 316 °C | 550 - 600 °F | |
| Middle Barrel Temperature | 302 - 329 °C | 575 - 625 °F | |
| Front Barrel Temperature | 316 - 343 °C | 600 - 650 °F | |
| Nozzle Temperature | 316 - 343 °C | 600 - 650 °F | |
| Melt Temperature | 316 - 343 °C | 600 - 650 °F | |
| Mold Temperature | 10.0 - 93.3 °C | 50.0 - 200 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.276 - 0.689 MPa | 40.0 - 100 psi | |
| Screw Speed | 25 - 75 rpm | 25 - 75 rpm |
Users viewing this material also viewed the following:
- DSM Akulon® K224-HG2U (Cond.) 10% Glass Reinforced Nylon 6 (North America) (discontinued **)
- Materion Brush 1915â„¢ Hard Temper Rod, 0.375" - 0.500"
- Chase Plastics CP Pryme® N300HL (Dry) Nylon 6, Heat Stabilized, Lubricated, Recycled Content
- Dalau Dalcon 021 75% Virgin PTFE, 25% Carbon Coke
- Polyram PlusTek PA124 Nylon 6.6, Injection Molding
- ExxonMobil Paxon™ AA60-003 Blow Molding Resin
- Epoxy Technology EPO-TEK® 320 Optical, Opaque Epoxy
- DuPont Teijin Films Melinex® 329 Polyester Film, 380 Gauge
- Eurostar Staramide BG7HU PA6, 35% Glass Fiber Filled, Heat and UV Stabilized, Injection Molded
Copyright © lookpolymers.com All Rights Reserved