SABIC Innovative Plastics LNP THERMOCOMP RF004XXD PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF004XXD PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RF004XXD is a compound based on Nylon 66 resin containing 20% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| 1.295 g/cc | 0.04678 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.800 % | 0.800 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0047 cm/cm @Time 86400 sec |
0.0047 in/in @Time 24.0 hour |
ISO 294 |
| 0.0050 cm/cm @Time 86400 sec |
0.0050 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.012 cm/cm @Time 86400 sec |
0.012 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0124 cm/cm @Time 86400 sec |
0.0124 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 156 MPa | 22600 psi | ASTM D638 |
| 159 MPa | 23100 psi | ISO 527 | |
| Elongation at Break | 3.6 % | 3.6 % | ASTM D638 |
| 3.7 % | 3.7 % | ISO 527 | |
| Tensile Modulus | 7.17 GPa | 1040 ksi | 50 mm/min; ASTM D638 |
| 7.30 GPa | 1060 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 230 MPa | 33400 psi | ASTM D790 |
| 241 MPa | 35000 psi | ISO 178 | |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| 7.00 GPa | 1020 ksi | ISO 178 | |
| Izod Impact, Notched | 1.01 J/cm | 1.89 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.33 J/cm | 15.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 56.0 kJ/m² | 26.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.68 | 0.68 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 161 x 10-8 mm³/N-M | 80.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 38.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
21.6 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 79.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 79.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
44.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 221 °C | 430 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 247 °C @Thickness 3.20 mm |
477 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Arlon 31580R015 0.015" (0.381 mm) Uncured Unsupported Silicone Rubber on an HDPE Carrier (discontinued *
- Lotte Chemical Titan TITANPRO® 6531M Polypropylene homopolymer
- Henkel Turco T-4181L Liquid Alkaline Rust Remover
- Vyncolit X655 Novolac Phenolic
- A. Schulman PP 1667-01 Polypropylene Natural Homopolymer Polypropylene
- ChevronTexaco Vistac® ISO 220 Way Oil
- Fainplast Compounds HAX HF 4121 Halogen Free PVC
- Fainplast Compounds PG 60/C Flexible PVC, Extrusion Modified with Rubber
- PSM Industries Pacific Sintered Metals High Strength Nickel Steel FN-262-S Powdered Metal
Copyright © lookpolymers.com All Rights Reserved