SABIC Innovative Plastics NORYL 731S PPE+PS (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics NORYL 731S PPE+PS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High heat PPO/HIPS alloy suitable for use in some potable water applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.08 g/cc | 1.08 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Time 86400 sec |
0.060 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 30 % | 30 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.42 GPa | 351 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 2.08 J/cm | 3.90 ft-lb/in | ASTM D256 |
| 1.33 J/cm @Temperature -40.0 °C |
2.49 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 130 µm/m-°C @Temperature -40.0 - 60.0 °C |
72.2 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 117 °C @Thickness 3.20 mm |
243 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 126 °C @Thickness 6.40 mm |
259 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 90.0 °C | 194 °F | UL 746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CM6240 PC+ABS (Asia Pacific)
- M. Holland Company AB103LG ABS Acrylonitrile Butadiene Styrene
- H.C. Starck Glass Melting Electrodes made from Electron Beam Melted Molybdenum
- Techmer ES Plaslube® J-4/30/TF/13/SI/2 NAT PA6/12
- Plenco 6401 Phenolic, Briquette, Transfer Molded
- Toyobo PELPRENE™ S6002 Polyester TPE, Ultra Heat-resistant
- Du-Co Ceramics S-699 Alumina
- ERG Aerospace Duocel® Aluminum Metal Foam
- ExxonMobil Mobil Delvac 50 Synthetic Transmission Fluid
- BASF Ultramid® 8267G HS BK-106 15/25% Glass/Mineral Filled PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved