- Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1400°F (760°C)
Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1400°F (760°C)
| Category | Metal , Nonferrous Metal , Nickel Alloy , Superalloy |
| Manufacturer | Special Metals (includes the former Inco Alloys International Inc.) |
| Trade Name | INCONEL® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Special Metals INCONEL® 625LCF® Nickel Superalloy (UNS N06626) Annealed 2150°F (1180°C) + Aged 1400°F (760°C).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Tensile strength (ultimate and yield), elongation, and hardness values are for samples annealed 2150°F (1180°C)/5 minutes/AC + Aged 1400°F (760°C)/100h/AC. This produces ASTM grain size 5.0. Other property values are typical of this alloy.Data provided by the manufacturer, Special Metals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 8.44 g/cc | 0.305 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell B | 95 | 95 | |
| Tensile Strength, Ultimate | 836.3 MPa | 121300 psi | |
| Tensile Strength, Yield | 390 MPa @Strain 0.200 % |
56500 psi @Strain 0.200 % |
|
| Elongation at Break | 50 % | 50 % | |
| Modulus of Elasticity | 208 GPa | 30200 ksi | |
| Poissons Ratio | 0.28 | 0.28 | |
| Shear Modulus | 81.4 GPa | 11800 ksi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 12.8 µm/m-°C @Temperature 21.0 - 100 °C |
7.11 µin/in-°F @Temperature 69.8 - 212 °F |
Mean |
| 13.3 µm/m-°C @Temperature 21.0 - 300 °C |
7.39 µin/in-°F @Temperature 69.8 - 572 °F |
Mean | |
| 13.9 µm/m-°C @Temperature 21.0 - 500 °C |
7.72 µin/in-°F @Temperature 69.8 - 932 °F |
Mean | |
| 14.9 µm/m-°C @Temperature 21.0 - 700 °C |
8.28 µin/in-°F @Temperature 69.8 - 1290 °F |
Mean | |
| Specific Heat Capacity | 0.410 J/g-°C | 0.0980 BTU/lb-°F | |
| Thermal Conductivity | 9.70 W/m-K | 67.3 BTU-in/hr-ft²-°F | |
| Melting Point | 1290 - 1350 °C | 2350 - 2460 °F | |
| Solidus | 1290 °C | 2350 °F | |
| Liquidus | 1350 °C | 2460 °F | |
| Maximum Service Temperature, Air | 650 °C | 1200 °F | resistance to low cycle and thermal fatigue |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Aluminum, Al | <= 0.40 % | <= 0.40 % | |
| Carbon, C | <= 0.030 % | <= 0.030 % | |
| Chromium, Cr | 20 - 23 % | 20 - 23 % | |
| Cobalt, Co | <= 1.0 % | <= 1.0 % | |
| Iron, Fe | <= 5.0 % | <= 5.0 % | |
| Manganese, Mn | <= 0.50 % | <= 0.50 % | |
| Molybdenum, Mo | 8.0 - 10 % | 8.0 - 10 % | |
| Nickel, Ni | >= 58 % | >= 58 % | |
| Niobium, Nb (Columbium, Cb) | 3.15 - 4.15 % | 3.15 - 4.15 % | Includes Ta |
| Nitrogen, N | <= 0.020 % | <= 0.020 % | |
| Phosphorous, P | <= 0.015 % | <= 0.015 % | |
| Silicon, Si | <= 0.020 % | <= 0.020 % | |
| Sulfur, S | <= 0.015 % | <= 0.015 % | |
| Titanium, Ti | <= 0.40 % | <= 0.40 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000132 ohm-cm | 0.000132 ohm-cm | |
| Magnetic Permeability | 1.0006 | 1.0006 | at 200 Oersted (15.9 kA/m) |
Users viewing this material also viewed the following:
- Sylvin Technologies 9915-70 Natural PVC Molding Compound
- Samsung Cheil Industries Starex® BC-0140 H ABS, Unreinforced General Purpose
- UBE 7034T Nylon 6/12 Monofilament (Drawing Ratio=5.5, Diameter 0.4 mm)
- A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound
- A. Schulman POLYFORT™ FPP 1697HU High Flow Fortified Polypropylene
- 3M S60HS Glass Bubbles
- Polymer Resources PPX/NY G30 Modified PPO, 30% Glass Reinforced PPX/Nylon 6,6 Alloy (Unverified Data**)&l
- Mo-Sci Corporation GL-0237 Hollow Glass Spheres
Copyright © lookpolymers.com All Rights Reserved