- Solvay Technyl® A 218 V30 Nylon 66, 30% Glass Fiber, EH50
Solvay Technyl® A 218 V30 Nylon 66, 30% Glass Fiber, EH50
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Technyl® A 218 V30 Nylon 66, 30% Glass Fiber, EH50.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide PA66, reinforced with 30% of glass fiber, heat stabilized, for injection molding.Technyl A 218 V30 is used in all sectors of industry, offering an excellent combination between thermal and mechanical properties. This grade is commonly used in the automotive industry for engine components, such as water tanks, degassing and liquid containers, engine covers, and various housing.This product is available in natural, black and in colors on request.Information provided by Rhodia; Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183-A |
| Water Absorption | 0.80 % | 0.80 % | (Beginning Dry) 24 hours in water 23°C. ISO 62 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | RHODIA-EP |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | RHODIA-EP |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 135 MPa | 19600 psi | ISO 527 |
| Tensile Strength, Yield | 135 MPa | 19600 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 7.50 GPa | 1090 ksi | ISO 527 |
| Flexural Yield Strength | 175 MPa | 25400 psi | ISO 178 |
| Flexural Modulus | 5.90 GPa | 856 ksi | ISO 178 |
| Izod Impact Resistance | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 9.50 J/cm² | 45.2 ft-lb/in² | ISO 179/EU-1993 |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179/1EA-1993 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 263 °C | 505 °F | ISO 3146-C |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 93 |
| Dielectric Constant | 4.0 @Frequency 1e+6 Hz |
4.0 @Frequency 1e+6 Hz |
IEC 250 |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | IEC 243-1 |
| Dissipation Factor | 0.11 @Frequency 1e+6 Hz |
0.11 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 425 V | 425 V | IEC 112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 270 - 280 °C | 518 - 536 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F |
Users viewing this material also viewed the following:
- Pyrotek PROSILY G-10R Graphite Lubricant/Coating
- PolyOne Edgetek® LCP-30CF/000 Liquid Crystal Polymer - 30% Carbon Fiber (discontinued **)
- LG Chemical LUMID HI2302A(W) PA6+GF30%, High Impact
- Inno-Comp INNOPOL® CS 2-8960 60% Barium-Sulfate Filled Polypropylene Block-Copolymer
- Westlake Epolene® C-16P Coating Grade - Branched Medium Molecular Weight Polyethylene Polymer
- Asahi Kasei Xyron® 240Z Modified Polyphenylene Ether
- Nabaltec ACTILOX® B60 AlO(OH) Boehmite
- Beijing Evergrow Resources UHF-W400 UHMW PE Fiber
- Lanxess Pocan® B 3235 XF 000000 PBT, 30% Glass Fiber
Copyright © lookpolymers.com All Rights Reserved