Chosun Refractories HACT-170 High Alumina Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | Chosun Refractories HACT-170 High Alumina Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.002943 - 0.006867 GPa <br>@Temperature 110 °C,<br> Time 86400 sec |
0.4269 - 0.9960 ksi <br>@Temperature 230 °F,<br> Time 24.0 hour |
|
| 0.002943 - 0.006867 GPa <br>@Temperature 1000 °C,<br> Time 10800 sec |
0.4269 - 0.9960 ksi <br>@Temperature 1830 °F,<br> Time 3.00 hour |
||
| 0.003924 - 0.007848 GPa <br>@Temperature 1350 °C,<br> Time 10800 sec |
0.5691 - 1.138 ksi <br>@Temperature 2460 °F,<br> Time 3.00 hour |
||
| 0.004905 - 0.008829 GPa <br>@Temperature 1500 °C,<br> Time 10800 sec |
0.7114 - 1.281 ksi <br>@Temperature 2730 °F,<br> Time 3.00 hour |
||
| Compressive Strength | 19.6 - 29.4 MPa <br>@Temperature 110 °C,<br> Time 86400 sec |
2840 - 4270 psi <br>@Temperature 230 °F,<br> Time 24.0 hour |
Cold Crushing Strength |
| 19.6 - 29.4 MPa <br>@Temperature 1000 °C,<br> Time 10800 sec |
2840 - 4270 psi <br>@Temperature 1830 °F,<br> Time 3.00 hour |
Cold Crushing Strength | |
| 24.5 - 34.3 MPa <br>@Temperature 1350 °C,<br> Time 10800 sec |
3560 - 4980 psi <br>@Temperature 2460 °F,<br> Time 3.00 hour |
Cold Crushing Strength | |
| 29.4 - 39.2 MPa <br>@Temperature 1500 °C,<br> Time 10800 sec |
4270 - 5690 psi <br>@Temperature 2730 °F,<br> Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.82584 W/m-K <br>@Temperature 260 °C |
5.7220 BTU-in/hr-ft²-°F <br>@Temperature 500 °F |
|
| 0.89563 W/m-K <br>@Temperature 540 °C |
6.2056 BTU-in/hr-ft²-°F <br>@Temperature 1000 °F |
||
| 0.96542 W/m-K <br>@Temperature 800 °C |
6.6892 BTU-in/hr-ft²-°F <br>@Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1700 °C | 3090 °F | limited |
| Shrinkage | -0.350 % <br>@Temperature 1500 °C,<br> Time 10800 sec |
-0.350 % <br>@Temperature 2730 °F,<br> Time 3.00 hour |
|
| -0.200 % <br>@Temperature 1350 °C,<br> Time 10800 sec |
-0.200 % <br>@Temperature 2460 °F,<br> Time 3.00 hour |
||
| -0.0300 % <br>@Temperature 110 °C,<br> Time 86400 sec |
-0.0300 % <br>@Temperature 230 °F,<br> Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 65 % | 65 % | |
| SiO2 | 30 % | 30 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Material Required for Estimating(kg/?) | 2,350 | |
| Water Required for Casting(%) | 9.5 |
Users viewing this material also viewed the following:
- LyondellBasell Hostacomâ„¢ RE-44AC Thermoplastic Polyolefin Elastomer
- Sylvin Technologies 8915-70 Natural PVC Extrusion Compound
- Unifrax Fiberfrax® QF-180™ Coating Cement
- DuPont Performance Polymers Hytrel® DYM250S BK472 TPC-ET+PBT (Unverified Data**)
- Colorite Polymers 6507 General Purpose Vinyl Compound
- 3M 5903 Outdoor Masking Poly Tape
- Arlon CP-310R Bulk Compound
- Ametek Ultra 304L P/M Stainless Steel, Sintered from 6.75 g/cc Green Density
Copyright © lookpolymers.com All Rights Reserved