- HOME
- POLYMER SEARCH
- Thermoplastic
- Nylon
- Nylon 6
- Nylon 6, 60% Glass Fiber Filled
- Solvay TECHNYLSTARâ„¢ SX 218 V60 Black Z PA6, 60% glass filled, DRY
Solvay TECHNYLSTARâ„¢ SX 218 V60 Black Z PA6, 60% glass filled, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | TECHNYLSTAR™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYLSTARâ„¢ SX 218 V60 Black Z PA6, 60% glass filled, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYLSTAR Polyamide reinforced with 60% of glass fiber, heat stabilized, for injection molding. Characterized by a high fluidity of the melt. Available in: Asia Pacific, Europe and North AmericaProduct Applications: TECHNYL STAR SX 218 V60 BLACK Z is suitable for all applications where a high rigidity is required. Due to its outstanding flow properties, the material easily fills the mould and the surface aspect of the finished part is excellent.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in³ | ISO 1183/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 240 MPa | 34800 psi | ISO 527 Type 1A |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 Type 1A |
| Tensile Modulus | 21.0 GPa | 3050 ksi | ISO 527 Type 1A |
| Flexural Modulus | 19.0 GPa | 2760 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/1eA |
| Izod Impact, Unnotched (ISO) | 90.0 kJ/m² | 42.8 ft-lb/in² | ISO 180/1eU |
| Charpy Impact Unnotched | 8.50 J/cm² | 40.4 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 222 °C | 432 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 220 - 225 °C | 428 - 437 °F | |
| Front Barrel Temperature | 240 - 245 °C | 464 - 473 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 235-240°C |
Users viewing this material also viewed the following:
- S&E Specialty Polymers TufTech™ G-3570 PVC Compound
- Polimeri Europa Riblene® FF 39 Low Density Polyethylene - Blown Film Extrusion
- LNP Lubricomp® FL-4410 Polyetherimide, Silicone Lubricant Additive (discontinued **)
- Hong Kun Group UV 1130 UV Absorber
- LATI Latigloss 66 H2 G/60 PA 66, 60% Glass Fiber Reinforced, Heat Stabilized
- Stir SpA C 2036 DS AT (PVC)
- Unitika A3130HR-25 PA6, 25% Mineral Reinforced, Conditioned
- TriStar Ultracomp UC-400 Composite Bearing
- Arlon 55578R036 0.036" (0.914 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- 3M Dyneon™ 81TZ High Temperature Perfluoroelastomer
Copyright © lookpolymers.com All Rights Reserved