SABIC Innovative Plastics Xenoy® 5720U PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Xenoy® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Xenoy® 5720U PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Unfilled PBT+PC alloy. Outstanding low temperature impact/chemical resistance. UV stabilized version of XENOY
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.17 g/cc | 1.17 g/cc | ASTM D792 |
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| 1.17 g/cc | 0.0423 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.28 % | 0.28 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.010 - 0.012 cm/cm @Thickness 3.20 mm |
0.010 - 0.012 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| 3.8 g/10 min @Load 2.16 kg, Temperature 250 °C |
3.8 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 | |
| 6.0 g/10 min @Load 2.16 kg, Temperature 265 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 | |
| 11 g/10 min @Load 5.00 kg, Temperature 250 °C |
11 g/10 min @Load 11.0 lb, Temperature 482 °F |
ISO 1133 | |
| 11.4 g/10 min @Load 5.00 kg, Temperature 250 °C |
11.4 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 | |
| 19.7 g/10 min @Load 5.00 kg, Temperature 266 °C |
19.7 g/10 min @Load 11.0 lb, Temperature 511 °F |
ASTM D1238 | |
| Melt Index of Compound | 3.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 6.0 g/10 min @Load 2.16 kg, Temperature 265 °C |
6.0 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 | |
| 10 g/10 min @Load 5.00 kg, Temperature 250 °C |
10 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 | |
| 18 g/10 min @Load 5.00 kg, Temperature 265 °C |
18 g/10 min @Load 11.0 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 43.0 MPa | 6240 psi | 5 mm/min; ISO 527 |
| 43.0 MPa | 6240 psi | 50 mm/min; ISO 527 | |
| 47.0 MPa | 6820 psi | Type I, 10 mm/min; SABIC - Japan Method | |
| 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D638 | |
| 50.0 MPa | 7250 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | 5 mm/min; ISO 527 |
| 44.0 MPa | 6380 psi | Type I, 5 mm/min; ASTM D638 | |
| 45.0 MPa | 6530 psi | Type I, 10 mm/min; SABIC - Japan Method | |
| 47.0 MPa | 6820 psi | 50 mm/min; ISO 527 | |
| 47.0 MPa | 6820 psi | Type I, 50 mm/min; ASTM D638 | |
| Elongation at Break | 106.8 % | 106.8 % | 5 mm/min; ISO 527 |
| 109.5 % | 109.5 % | Type I, 10 mm/min; SABIC - Japan Method | |
| 115.3 % | 115.3 % | 50 mm/min; ISO 527 | |
| 116.6 % | 116.6 % | Type I, 50 mm/min; ASTM D638 | |
| 122.4 % | 122.4 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 50 mm/min; ASTM D638 |
| 4.1 % | 4.1 % | 5 mm/min; ISO 527 | |
| 4.6 % | 4.6 % | 50 mm/min; ISO 527 | |
| 4.6 % | 4.6 % | Type I, 5 mm/min; ASTM D638 | |
| 4.6 % | 4.6 % | Type I, 10 mm/min; SABIC - Japan Method | |
| Tensile Modulus | 1.79 GPa | 260 ksi | 1 mm/min; ISO 527 |
| 1.81 GPa | 263 ksi | 50 mm/min; ASTM D638 | |
| 1.83 GPa | 265 ksi | 5 mm/min; ASTM D638 | |
| 1.83 GPa | 265 ksi | 10 mm/min; SABIC - Japan Method | |
| Flexural Strength | 69.0 MPa | 10000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 70.0 MPa | 10200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 71.0 MPa | 10300 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 1.66 GPa | 241 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 1.86 GPa | 270 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 7.22 J/cm | 13.5 ft-lb/in | ASTM D256 |
| 5.98 J/cm @Temperature -40.0 °C |
11.2 ft-lb/in @Temperature -40.0 °F |
ASTM D256 | |
| 6.47 J/cm @Temperature -30.0 °C |
12.1 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 6.63 J/cm @Temperature -10.0 °C |
12.4 ft-lb/in @Temperature 14.0 °F |
ASTM D256 | |
| 6.91 J/cm @Temperature 0.000 °C |
12.9 ft-lb/in @Temperature 32.0 °F |
ASTM D256 | |
| 6.95 J/cm @Temperature -20.0 °C |
13.0 ft-lb/in @Temperature -4.00 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*4; ISO 180/1A |
| 46.0 kJ/m² @Temperature -40.0 °C |
21.9 ft-lb/in² @Temperature -40.0 °F |
80*10*4; ISO 180/1A | |
| 48.0 kJ/m² @Temperature -30.0 °C |
22.8 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| 50.0 kJ/m² @Temperature -20.0 °C |
23.8 ft-lb/in² @Temperature -4.00 °F |
80*10*4; ISO 180/1A | |
| 52.0 kJ/m² @Temperature -10.0 °C |
24.7 ft-lb/in² @Temperature 14.0 °F |
80*10*4; ISO 180/1A | |
| 55.0 kJ/m² @Temperature 0.000 °C |
26.2 ft-lb/in² @Temperature 32.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 5.50 J/cm² | 26.2 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| 4.70 J/cm² @Temperature -30.0 °C |
22.4 ft-lb/in² @Temperature -22.0 °F |
Edgew 80*10*4 sp=62mm; ISO 179/1eA | |
| Dart Drop, Total Energy | 44.0 J | 32.5 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 41.0 J @Temperature -20.0 °C |
30.2 ft-lb @Temperature -4.00 °F |
Instrumented Impact, Energy @ peak, -20°C; ASTM D3763 | |
| 49.0 J @Temperature -30.0 °C |
36.1 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 | |
| 49.0 J @Temperature -40.0 °C |
36.1 ft-lb @Temperature -40.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 | |
| 53.0 J @Temperature -20.0 °C |
39.1 ft-lb @Temperature -4.00 °F |
ASTM D3763 | |
| 54.0 J @Temperature 23.0 °C |
39.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 | |
| 59.0 J @Temperature -40.0 °C |
43.5 ft-lb @Temperature -40.0 °F |
ASTM D3763 | |
| 61.0 J @Temperature -30.0 °C |
45.0 ft-lb @Temperature -22.0 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 97.5 µm/m-°C @Temperature -40.0 - 95.0 °C |
54.2 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
| 97.5 µm/m-°C @Temperature -30.0 - 80.0 °C |
54.2 µin/in-°F @Temperature -22.0 - 176 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 100 µm/m-°C @Temperature -40.0 - 95.0 °C |
55.6 µin/in-°F @Temperature -40.0 - 203 °F |
ASTM E 831 |
Users viewing this material also viewed the following:
- Network Polymers MS 150 Styrene Methyl Methacrylate Terpolymer
- Polymer Resources PC/ABS-GP1-[color]-LG General Purpose PC/ABS Alloy, Low Gloss Grade
- Ineos ABS Lustran® 248
- Minelco MicaFil Vermiculite
- Kostat BK-STAT P048BK PP Compound
- SABIC Innovative Plastics ULTEM 9075 PEI (Asia Pacific)
- 3M 9088FL High Performance Double Coated Tapes with Adhesive 375
- Asahi Kasei Thermylene® P1-25FM-Y175 25% Glass Fiber/ Mineral Reinforced
- Aclo Accutech Polypropylene Copolymer CP0436G25M5CL Glass/Mineral Reinforced Coupled
- Ashley Polymers Ashlene® 747 Nylon 6/66
Copyright © lookpolymers.com All Rights Reserved