- Solvay TECHNYL® R CR 218 V30 Nylon 6, 30% glass fiber, DRY
Solvay TECHNYL® R CR 218 V30 Nylon 6, 30% glass fiber, DRY
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | TECHNYL® R |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® R CR 218 V30 Nylon 6, 30% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
TECHNYL® CR 218 V30 is a polyamide 6, reinforced with 30% glass fiber, heat stabilized, for injection molding. It contains recycled raw materials. This product is available in black color.Benefits: The product offers a good combination between thermal and mechanical properties.Available in: Europe Applications: It is used in a wide variety of industries.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183/A |
| Linear Mold Shrinkage, Flow | 0.0037 cm/cm | 0.0037 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527 Type 1A |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 Type 1A |
| Tensile Modulus | 9.60 GPa | 1390 ksi | ISO 527 Type 1A |
| Flexural Modulus | 8.80 GPa | 1280 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.520 J/cm² | 2.47 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
ISO 1210 |
| Glow Wire Test | 650 °C | 1200 °F | ISO 60695-2-12 |
| 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 225 - 230 °C | 437 - 446 °F | |
| Mold Temperature | 80.0 - 100 °C | 176 - 212 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 230-240°C | |
| Mixing Zone | 240-250°C |
Users viewing this material also viewed the following:
- Quadrant EPP Ertalon® 6XAU+ PA 6, heat stabilized, cast (ISO Data)
- Teknor Apex Flexalloy® 3500-65 Polyvinyl Chloride Elastomer
- Williams Advanced Alloys WS186 Solder
- Ecomass® 1050ZD96 Tungsten Powder Filled Polyamide Alloy, Injection Molding Grade
- DuPont Performance Polymers Delrin® 527UV NC010 Acetal (POM) (Unverified Data**)
- ExxonMobil Santoprene® 8221-70 Thermoplastic Elastomer
- China Tungsten YT6S Tungsten Carbide
- Cotronics Duralco™ 128 500°F (260°C) Ceramic Filled Epoxy
- SABIC Innovative Plastics Cycoloy® CX1440 PC+ABS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved