Solvay TECHNYL® C 30H1 V30 Natural/F PA6, 30% glass fiber, DRY

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer Solvay
Trade Name Technyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay TECHNYL® C 30H1 V30 Natural/F PA6, 30% glass fiber, DRY.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Flame retardant polyamide PA6, reinforced with 30% of glass fiber, for injection molding.Available in: Asia Pacific, Europe, Latin America and North AmericaProduct Applications: This grade has good mechanical properties, flame retardant rating UL94 V0 and glow-wire at 960°C. It is specially suitable for pieces such as: switches, timers, etc. This product is available in Natural.Information provided by Rhodia, Rhodia has been acquired by Solvay.
Physical Properties Metric English Comments
Density 1.62 g/cc
0.0585 lb/in³
ISO 1183/A
Water Absorption 0.95 %

@Temperature 23.0 °C,
Time 86400 sec
 0.95 %

@Temperature 73.4 °F,
Time 24.0 hour
 ISO 62
Linear Mold Shrinkage 0.0075 cm/cm
0.0075 in/in
Isotropy
Linear Mold Shrinkage, Flow 0.0060 cm/cm
0.0060 in/in
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
Mechanical Properties Metric English Comments
Tensile Strength at Break 114 MPa
16500 psi
ISO 527 Type 1A
Elongation at Break 1.8 %
1.8 %
ISO 527 Type 1A
Tensile Modulus 11.4 GPa
1650 ksi
ISO 527 Type 1A
Charpy Impact Unnotched 3.70 J/cm²
17.6 ft-lb/in²
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²
4.28 ft-lb/in²
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
ISO 11357
Deflection Temperature at 1.8 MPa (264 psi) 197 °C
387 °F
ISO 75/Af
Flammability, UL94 V-0

@Thickness 0.800 mm
 V-0

@Thickness 0.0315 in
 1210
V-0

@Thickness 1.60 mm
 V-0

@Thickness 0.0630 in
 1210
V-0

@Thickness 3.20 mm
 V-0

@Thickness 0.126 in
 1210
Glow Wire Test 825 °C

@Thickness 0.800 mm
 1520 °F

@Thickness 0.0315 in
 ignition temperature; ISO 60695-2-13
850 °C

@Thickness 1.60 mm
 1560 °F

@Thickness 0.0630 in
 ignition temperature; ISO 60695-2-13
960 °C

@Thickness 0.800 mm
 1760 °F

@Thickness 0.0315 in
 ISO 60695-2-12
960 °C

@Thickness 1.60 mm
 1760 °F

@Thickness 0.0630 in
 ISO 60695-2-12
Electrical Properties Metric English Comments
Dielectric Strength 41.0 kV/mm
1040 kV/in
IEC 60243
Dissipation Factor 0.010
0.010
IEC 60250
Comparative Tracking Index 450 V
450 V
Solution A; IEC 60112
Processing Properties Metric English Comments
Feed Temperature 230 - 240 °C
446 - 464 °F
Front Barrel Temperature 240 - 255 °C
464 - 491 °F
Mold Temperature 80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 °C
176 °F
Moisture Content <= 0.20 %
<= 0.20 %
Descriptive Properties Value Comments
Compression Zone 240-250°C
Users viewing this material also viewed the following: