Polyram Polytron P50B07 Polypropylene, 50% Long Glass Fiber, UV Stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 50% Glass Fiber Filler |
| Manufacturer | Polyram |
| Trade Name | Polytron |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram Polytron P50B07 Polypropylene, 50% Long Glass Fiber, UV Stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
A chemically coupled 50% long glass fiber reinforced black polypropylene, heat stabilized, UV stabilized for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 135 MPa | 19600 psi | ISO 527 |
| Elongation at Break | 1.7 % | 1.7 % | ISO 527 |
| Tensile Modulus | 12.9 GPa | 1870 ksi | ISO 527 |
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 2.20 J/cm² | 10.5 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 167 °C | 333 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 159 °C | 318 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Flame Spread | 20 mm/min | 0.79 in/min | FMVSS302 |
Users viewing this material also viewed the following:
- Nilit FRIANYL B63 KG30 Nylon 6 for injection molding, 30% chalk filled
- Micropol Microlin ML27 Linear Polyethylene Rotational Molding Powder
- Shakespeare CL-10XT Super Tough Nylon Copolymer Fishing Line, 20 lb
- Shin-Etsu Silicones KF-9003 Fluid
- Saint-Gobain Chemlam® XF-900 Fully Sintered PTFE Coated, Flexible, Non-porous Fluoropolymer Laminated Composite
- Tra-Con Tra-Cast 3012 Clear Epoxy Casting Compound
- A. Schulman POLYBATCH™ Green 3011E Concentrate Based In Polyethylene
- DuPont Teijin Films Melinex® 693 Polyester Film
- Eurostar Staramide BT6 PA6, 30% Mineral Filled, Injection Molded
- Polyplastic Armamid® PA6 GF 30-2HSM-902 Nylon, 30% Glass Filled
Copyright © lookpolymers.com All Rights Reserved