ExxonMobil Santoprene® 111-80 Thermoplastic Elastomer (discontinued **)

Category	Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Santoprene® 111-80 Thermoplastic Elastomer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

A soft, black, versatile thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in a wide range of injection molding applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding. It is polyolefin based and completely recyclable.Recommended for applications requiring excellent flex fatigue resistance.Recommended for applications requiring excellent ozone resistance.Designed for applications requiring high-flow materials.Recommended for applications requiring superior part surface appearance.Information provided by Advanced Elastomer Systems

Physical Properties	Metric	English	Comments
Specific Gravity	0.970 g/cc	0.970 g/cc	23°C; ASTM D792

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	80	80	.12 in; ASTM D2240
Tensile Strength at Break	9.38 MPa	1360 psi	Across Flow; ASTM D412
Tensile Strength, Ultimate	4.41 MPa	640 psi	Across Flow; ASTM D412
Elongation at Break	460 %	460 %	Across Flow; ASTM D412
Compression Set	38 %	38 %	73°F, 70 hr; ASTM D395
	64 %	64 %	257°F, 70 hr; ASTM D395

Thermal Properties	Metric	English	Comments
Brittleness Temperature	-55.0 °C	-67.0 °F	ASTM D746

Electrical Properties	Metric	English	Comments
Dielectric Constant	2.7	2.7	ASTM D150
Dielectric Strength	29.5 kV/mm	750 kV/in	ASTM D149

Processing Properties	Metric	English	Comments
Processing Temperature	175 - 230 °C	347 - 446 °F
Rear Barrel Temperature	177 - 193 °C	350 - 380 °F
Middle Barrel Temperature	179 - 199 °C	355 - 390 °F
Front Barrel Temperature	179 - 204 °C	355 - 400 °F
Nozzle Temperature	191 - 229 °C	375 - 445 °F
Melt Temperature	193 - 241 °C	380 - 465 °F	Processing
Mold Temperature	10.0 - 51.7 °C	50.0 - 125 °F	Processing
Drying Temperature	82.2 °C	180 °F
Dry Time	3 hour	3 hour
Moisture Content	0.080 %	0.080 %
Back Pressure	0.345 - 0.689 MPa	50.0 - 100 psi	Processing
Clamp Pressure	41.4 - 68.9 MPa	6000 - 10000 psi
Vent Depth	0.00254 cm	0.00100 in
Cushion	0.317 - 0.635 cm	0.125 - 0.250 in
Screw Speed	100 - 200 rpm	100 - 200 rpm

Descriptive Properties	Value	Comments
Color	Black
Form	Pellets
Injection Rate	Fast
Maximum Regrind %	20
Screw Compression Ratio	2:1 - 2.5:1
Screw L/D Ratio	16:1 - 20:1