Solvay TECHNYL® C 236SI PA6, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® C 236SI PA6, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Unreinforced polyamide 6 with high impact strength for injection molding.Available in: Europe and North AmericaProduct Applications: TECHNYL® C 236SI has high impact strength and flexibility. This grade is suitable for power tools, sports goods, furniture and machine components. This product is available in natural, black and in colors on request.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ISO 1183/A |
| Water Absorption | 1.27 % @Temperature 23.0 °C, Time 86400 sec |
1.27 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0099 cm/cm | 0.0099 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0146 cm/cm | 0.0146 in/in | ISO 294-4 |
| 0.0206 cm/cm | 0.0206 in/in | ||
| Linear Mold Shrinkage, Transverse | 0.0186 cm/cm | 0.0186 in/in | ISO 294-4 |
| 0.0207 cm/cm | 0.0207 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 47.0 MPa | 6820 psi | ISO 527 Type 1A |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | ISO 527 type 1 A |
| Elongation at Break | 55 % | 55 % | ISO 527 Type 1A |
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527 type 1 A |
| Tensile Modulus | 2.20 GPa | 319 ksi | ISO 527 Type 1A |
| Flexural Strength | 77.0 MPa | 11200 psi | ISO 178 |
| Flexural Modulus | 1.93 GPa | 280 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 66.0 kJ/m² | 31.4 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 1.60 J/cm² @Temperature -30.0 °C |
7.61 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 7.60 J/cm² @Temperature 23.0 °C |
36.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 56.0 °C | 133 °F | ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 240 - 280 °C | 464 - 536 °F | |
| Front Barrel Temperature | 260 - 280 °C | 500 - 536 °F | |
| Mold Temperature | 80.0 °C | 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 240-280°C |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable 3201-xx05D Polyvinyl Chloride, Flexible (PVC, Flexible)
- Polymer Resources NY66-G43-[color]H Nylon, 43% Glass Reinforced, Heat Stabilized (DAM)
- Kazanorgsintez Process Oxygen, Gaseous
- Latrobe DuraTechâ„¢ 20CV Powder Metal Stainless Tool Steel
- Teknor Apex Uniprene® UN-2598D Thermoplastic Vulcanizate
- A. Schulman POLYFORT™ FPP 2121UV-M-31 Black Filled Polypropylene Homopolymer
- Dow Corning SILASTIC® 7-6840 BIOMEDICAL GRADE LSR, KIT
- Crucible Steel 21-4NNb Martensitic Steel
- Dow DS6D81 Polypropylene Random Copolymer Resin
- Dow Corning Z-6020 SILANE
Copyright © lookpolymers.com All Rights Reserved