PolyOne Geon™ L4605 Green 5765 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid)
| Category | Polymer , Thermoplastic , Vinyl (PVC) , PVC, Rigid Grade |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ L4605 Green 5765 Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 31.2 MPa | 4530 psi | 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 1.93 GPa | 280 ksi | 5.1 mm/min; ASTM D638 |
| Flexural Yield Strength | 55.9 MPa | 8110 psi | 13 mm/min; ASTM D790 |
| Flexural Modulus | 1.91 GPa | 277 ksi | 13 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.370 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.693 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Compression Molded; ASTM D256 |
| Dart Drop Total Energy | 69.4 J/cm @Temperature 23.0 °C |
0.130 ft-lb/mil @Temperature 73.4 °F |
extruded profile, Procedure A, C.125; ASTM D4226 |
| >= 178 J/cm @Temperature 23.0 °C |
>= 0.333 ft-lb/mil @Temperature 73.4 °F |
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 75.0 µm/m-°C | 41.7 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 42.2 °C @Thickness 3.18 mm |
108 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| 42.8 °C @Thickness 3.18 mm |
109 °F @Thickness 0.125 in |
Unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 36.1 °C @Thickness 3.18 mm |
97.0 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| 38.9 °C @Thickness 3.18 mm |
102 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 5.0 - 30 % | 5.0 - 30 % | 60°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 - 193 °C | 360 - 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | Medium Gloss | |
| Forms | Pellets | |
| Generic Material | PVC, Semi-Rigid | |
| Generic Name | Polyvinyl Chloride, Semi-Rigid (PVC, Semi-Rigid) | |
| Processing Method | Coextrusion | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Capstock | |
| Outdoor Applications |
Users viewing this material also viewed the following:
- Plansee WL20 Lanthanum Oxide-doped Tungsten
- SABIC Innovative Plastics Cycoloy® XCY630 PC+ABS (Europe-Africa-Middle East)
- Ravago Manufacturing Americas Enviramid™ N2340MHL BK Post Consumer Recycle Nylon 6, 40% Mineral Filled
- Lanxess Durethan® BKV 130 DUS008 901510 Nylon 6, Glass Fiber Reinforced, Impact Modified
- SABIC Innovative Plastics Valox® 830 PBT
- Trelleborg Emerson & Cuming Eccobond® 15 Variable Hardness Catalyst
- CP-Polymer-Technik Wellamid® 6000 MRGV 20/10 HWCP 20% Mineral and 10% Glass Fiber Nylon 6, Heat Stabilized, Conditioned
- Asahi Glass Fluon® PB1205 20% Glass Fiber, 5% Graphite, PTFE Filled Compound
- Axiall 01540 Plenum Flexible PVC
Copyright © lookpolymers.com All Rights Reserved