Solvay TECHNYL® A 218 V50 PA66, 50% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 50% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218 V50 PA66, 50% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: TECHNYL® A 218 V50 is a polyamide 66, reinforced with 50% of glass fiber, heat stabilized, for injection molding. This product is available in natural and black colors.Benefits: The product offers an excellent combination between thermal and mechanical properties.Available in: Asia Pacific, Europe and North AmericaRegulations compliance: Grades produced or imported in Europe comply with directive 453/2010/EC, which amends REACH directive 1907/2006/EC. This grade complies with RoHS directive 2002/95/EC. Unless specified, this grade is not suitable for food contact, medical devices or toy applications.Applications: It is used in a wide variety of industries.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in³ | ISO 1183/A |
| Water Absorption | 0.60 % @Temperature 23.0 °C, Time 86400 sec |
0.60 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Viscosity | 20 cP @Shear Rate 1000 1/s, Temperature 280 °C |
20 cP @Shear Rate 1000 1/s, Temperature 536 °F |
shear rate: 1000/s |
| 20 cP @Shear Rate 1000 1/s, Temperature 290 °C |
20 cP @Shear Rate 1000 1/s, Temperature 554 °F |
shear rate: 1000/s | |
| 20 cP @Shear Rate 1000 1/s, Temperature 300 °C |
20 cP @Shear Rate 1000 1/s, Temperature 572 °F |
shear rate: 1000/s | |
| 170 cP @Shear Rate 100 1/s, Temperature 300 °C |
170 cP @Shear Rate 100 1/s, Temperature 572 °F |
shear rate: 100/s | |
| 180 cP @Shear Rate 100 1/s, Temperature 290 °C |
180 cP @Shear Rate 100 1/s, Temperature 554 °F |
shear rate: 100/s | |
| 190 cP @Shear Rate 100 1/s, Temperature 280 °C |
190 cP @Shear Rate 100 1/s, Temperature 536 °F |
shear rate: 100/s | |
| 320 cP @Shear Rate 10.0 1/s, Temperature 300 °C |
320 cP @Shear Rate 10.0 1/s, Temperature 572 °F |
shear rate: 10/s | |
| 400 cP @Shear Rate 10.0 1/s, Temperature 290 °C |
400 cP @Shear Rate 10.0 1/s, Temperature 554 °F |
shear rate: 10/s | |
| 450 cP @Shear Rate 10.0 1/s, Temperature 280 °C |
450 cP @Shear Rate 10.0 1/s, Temperature 536 °F |
shear rate: 10/s | |
| Linear Mold Shrinkage | 0.0055 cm/cm | 0.0055 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0044 cm/cm | 0.0044 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 220 MPa | 31900 psi | ASTM D638 |
| 240 MPa | 34800 psi | ISO 527 Type 1A | |
| Tensile Stress | 155 MPa @Strain 1.00 % |
22500 psi @Strain 1.00 % |
|
| 240 MPa @Strain 2.00 % |
34800 psi @Strain 2.00 % |
||
| Elongation at Break | 2.0 % | 2.0 % | ISO 527 Type 1A |
| 2.0 % | 2.0 % | ASTM D638 | |
| Tensile Modulus | 16.2 GPa | 2350 ksi | ISO 527 Type 1A |
| Flexural Strength | 350 MPa | 50800 psi | ASTM D790 |
| Flexural Modulus | 13.5 GPa | 1960 ksi | ISO 178 |
| 13.8 GPa | 2000 ksi | ASTM D790 | |
| Izod Impact, Notched | 1.80 J/cm | 3.37 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 14.5 kJ/m² | 6.90 ft-lb/in² | ISO 180/1eA |
| Charpy Impact Unnotched | 9.50 J/cm² | 45.2 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 1.60 J/cm² | 7.61 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
8.33 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75/Af |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
1210 |
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
1210 | |
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
1210 | |
| Oxygen Index | 23 % | 23 % | ISO 4589 |
| Glow Wire Test | 650 °C @Thickness 0.800 mm |
1200 °F @Thickness 0.0315 in |
ISO 60695-2-12 |
| 650 °C @Thickness 1.60 mm |
1200 °F @Thickness 0.0630 in |
ISO 60695-2-12 | |
| 700 °C @Thickness 3.20 mm |
1290 °F @Thickness 0.126 in |
ISO 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 6.00e+14 ohm | 6.00e+14 ohm | IEC 60093 |
| Dielectric Constant | 3.7 | 3.7 | IEC 60250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243 |
| Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 265 - 275 °C | 509 - 527 °F | |
| Mold Temperature | 80.0 - 110 °C | 176 - 230 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C | |
| Mixing Zone | 280-290°C |
Users viewing this material also viewed the following:
- Pyrotek Pyrocast L-40 Insulating Refractory
- Radici Radilon® A 38 (cond.) Nylon 66
- BASF Capron® 5202 HS BK-102 Nylon 66 (Dry) (discontinued **)
- Lanxess Pocan® B 3233 HR 000000 Polybutylene Terephthalate, 30% Glass Fibers
- LG Chemical LUPOL GP3156F Flame Retardant PP
- SABIC Innovative Plastics ULTEM CRS5201R PEI (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ CE-505-B Concentrate Based In Polyethylene
- Haynes 25 alloy, room temperature after 15% cold reduction
- SABIC Innovative Plastics NORYL CN5246 PPE+PS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved