- Solvay TECHNYL® A 218 V25 Natural B PA66, 25% glass fiber, DRY
Solvay TECHNYL® A 218 V25 Natural B PA66, 25% glass fiber, DRY
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Solvay |
| Trade Name | Technyl® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay TECHNYL® A 218 V25 Natural B PA66, 25% glass fiber, DRY.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Polyamide 66, reinforced with 25% of glass fiber, specially stabilized to improve its resistance to oils and greases, for injection molding.Available in: EuropeProduct Applications: This product is recommended for molded parts exposed to high temperatures and in contact with oils and greases. Bearing housings are a typical example for which this formulation is suitable. TECHNYL® A 218 V25 is approved by major bearing manufacturers. This product is available in natural.Information provided by Rhodia, Rhodia has been acquired by Solvay.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | ISO 1183/A |
| Water Absorption | 0.90 % @Temperature 23.0 °C, Time 86400 sec |
0.90 % @Temperature 73.4 °F, Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage | 0.0047 cm/cm | 0.0047 in/in | Isotropy |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0085 cm/cm | 0.0085 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 179 MPa | 26000 psi | ISO 527 Type 1A |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 Type 1A |
| Tensile Modulus | 8.70 GPa | 1260 ksi | ISO 527 Type 1A |
| Flexural Strength | 280 MPa | 40600 psi | ISO 178 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ISO 178 |
| Charpy Impact Unnotched | 6.50 J/cm² | 30.9 ft-lb/in² | ISO 179/1eU |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 27.0 µm/m-°C @Temperature 23.0 - 85.0 °C |
15.0 µin/in-°F @Temperature 73.4 - 185 °F |
ISO 11359 |
| Melting Point | 263 °C | 505 °F | ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75/Af |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Front Barrel Temperature | 280 - 290 °C | 536 - 554 °F | |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Moisture Content | <= 0.20 % | <= 0.20 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Compression Zone | 270-280°C |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Z85T Hydrogenated NBR Compound
- Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 13% Plasticizer (discontinued **)
- Huntsman AroCy XU 71787.02 L Cyanate Ester
- KKPC Kuhmo HF 402 Flame Retarded General Purpose HIPS
- Indium Corp. Indalloy 114 Tin-Lead Solder Alloy
- Haynes Hastelloy® alloy 188 12.7 mm plate weldments
- Sichuan Deyang Haton® hFR70 PPS / AR Polyphenylene Sulfide
- Westlake Epolene® C-19 Coating Grade - Highly Branched Medium Molecular Weight Polyethylene Polymer, Maleation Processed
- Colorite Polymers 8804 General Purpose Vinyl Compound
- Unifrax Fiberfrax® Moist Pak-D® Ceramic Fiber Insulator
Copyright © lookpolymers.com All Rights Reserved