Solvay Specialty Polymers Solef® 21510 Polyvinylidene Fluoride (PVDF)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Solef® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 21510 Polyvinylidene Fluoride (PVDF).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 21510 PVDF copolymer has medium viscosity and is suitable for extrusion and for solution processing in lithium batteries applications.Features: Copolymer; Good Flexibility; Medium ViscosityAdditional Properties: Crystallization Heat - ASTM D3417 20.0 to 24.0 J/g; Heat of Fusion - ASTM D3417 20.0 to 24.0 J/gInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 - 1.80 g/cc | 0.0632 - 0.0650 lb/in³ | ASTM D792 |
| Water Absorption | <= 0.040 % @Time 86400 sec |
<= 0.040 % @Time 24.0 hour |
ISO 62 |
| Melt Flow | 3.0 - 9.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
3.0 - 9.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 20.0 - 40.0 MPa @Thickness 2.00 mm |
2900 - 5800 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 15.0 - 18.0 MPa @Thickness 2.00 mm |
2180 - 2610 psi @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
| Elongation at Break | 600 - 750 % @Thickness 2.00 mm |
600 - 750 % @Thickness 0.0787 in |
50 mm/min; ASTM D638 |
| Elongation at Yield | 12 - 15 % | 12 - 15 % | 50 mm/min; ASTM D638 |
| Tensile Modulus | 0.360 - 0.480 GPa @Thickness 2.00 mm |
52.2 - 69.6 ksi @Thickness 0.0787 in |
1.0 mm/min; ASTM D638 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 130 - 136 °C | 266 - 277 °F | DSC |
| Crystallization Temperature | 89.0 - 93.0 °C | 192 - 199 °F | Peak; ASTM D3418 |
| Glass Transition Temp, Tg | -40.0 °C | -40.0 °F | ASTM E1356 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Processing Technique | Extrusion; Solution Processing |
Users viewing this material also viewed the following:
- DuPont Bynel® 3062 Anhydride-Modified Ethylene Vinyl Acetate Adhesive Resin (discontinued **)
- Lucite International Colacryl ® TS2082 Acrylic Resin
- Momentive Performance Materials RTV6703 Black Adhesive Sealant, General Purpose Paste
- Teknor Apex Uniprene® UN-7100-40D Thermoplastic Vulcanizate
- UBE UBESTA® 3030U Nylon 12 (After Saturate Sodium Chloride for 500 hours)
- Ecomass® 4703ZD88 Tungsten Filled Polyurethane
- Dow BETAMATE™ 7205 Polyurethane Prepolymer
- Colorite Polymers CS8039UL Wire and Cable Insulation Vinyl Compound
- Eagle Brass 101 OFE COPPER (Certified), Spring
- Total PSI 975E Polystyrene
Copyright © lookpolymers.com All Rights Reserved