Polyram PlusTek RD104 Nylon 12, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 12 |
| Manufacturer | Polyram |
| Trade Name | PlusTek |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram PlusTek RD104 Nylon 12, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Outstanding flexibility polyamide 12 for injection molding applications.Information provided by Polyram Ram On Ind.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | DIN 53479 |
| Water Absorption | 0.90 % | 0.90 % | DIN 53495 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 80 | 80 | ASTM-D785 |
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | ASTM-D638 |
| Elongation at Break | 300 % | 300 % | ASTM-D638 |
| Tensile Modulus | 0.700 GPa | 102 ksi | ASTM-D790 |
| Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
| Flexural Modulus | 0.700 GPa | 102 ksi | ASTM-D790 |
| Izod Impact, Notched | 9.99 J/cm @Temperature 23.0 °C |
18.7 ft-lb/in @Temperature 73.4 °F |
ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 175 °C | 347 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | DIN 53461 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Glow Wire Test | 650 °C | 1200 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | DIN 53482 |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | DIN 53482 |
| Dielectric Strength | 55.0 kV/mm | 1400 kV/in | VDE 0303/4 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1182T PC Copolymer (Europe-Africa-Middle East)
- Huntsman PE 1008 Film Extrusion Polyethylene (discontinued **)
- Karina 42/7-FC-LMP Red Color Concentrate for PVC
- Zhejiang Juner PA66-301-G0 Flame-Retardant & Glass Reinforced, Non-Halogen PA66
- Elektro-Isola G-Etronax B Phenolic, Glass Fabric Reinforcement, Dark Brown, Tubes
- CIMBAR BARIMITE™ 200 High Purity Barite (BaSO4)
- Arlon 10842S090 Fully Cured, Unsupported Silicone Rubber
- Arlon 51986R020 0.020" (0.508 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
- Grupo Repol Dinalon® B2S35 V2-7035 PA6 High Viscosity, V2 Halogen Free, RAL 7035
Copyright © lookpolymers.com All Rights Reserved