- Solvay Specialty Polymers Omnix® FC-9050 Polyamide, High Performance (HPPA), 50% Glass Fiber
Solvay Specialty Polymers Omnix® FC-9050 Polyamide, High Performance (HPPA), 50% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Omnix® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Omnix® FC-9050 Polyamide, High Performance (HPPA), 50% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Omnix® FC-9050 is a 50% glass-fiber reinforced high-performance polyamide. It is hot-water moldable and intended for use in components requiring superior mechanical properties even after moisture absorption. Omnix® FC-9050 is characterized by high stiffness and strength, very good impact properties, good dimensional stability and high flow properties. This material is an economical alternative for food service applications using die-cast alloys.Features: Fast Molding Cycle; Good Dimensional Stability; Good Impact Resistance; Good Surface Finish; High Flow; High Stiffness; High Strength; Hot Water Moldability; PaintableUses: Appliances; Food Service ApplicationsInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Filler Content | 50 % | 50 % | Glass Fiber |
| Water Absorption | 0.27 % @Time 86400 sec |
0.27 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 235 MPa | 34100 psi | ISO 527-2 |
| Elongation at Break | 2.1 % | 2.1 % | ISO 527-2 |
| Tensile Modulus | 17.0 GPa | 2470 ksi | ISO 527-2 |
| Flexural Strength | 340 MPa | 49300 psi | ISO 178 |
| Flexural Modulus | 1.50 GPa | 218 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | Type 1, Notch A; ISO 180 |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 11357-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | Unannealed; ISO 75-2/A |
| Flammability, UL94 | HB | HB |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 250 °C | 482 °F | |
| Front Barrel Temperature | 285 °C | 545 °F | |
| Melt Temperature | 275 - 290 °C | 527 - 554 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 14400 - 43200 sec |
176 °F @Time 4.00 - 12.0 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Asia Pacific | |
| Europe | ||
| North America | ||
| Color | Black; Natural | |
| Form | Pellets | |
| Part Marking Code | >PAMXD6/66-GF50< | ISO 11469 |
| Processing Technique | Injection Molding; Water-Heated Mold Injection Molding | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- PEAK Werkstoff DISPAL S226 Aluminum Alloy, AlSi30CuMg, Condition T6
- ExxonMobil Santoprene® 111-64 Thermoplastic Elastomer (discontinued **)
- Lendell Manufacturing SRF-1 Foam
- Michelman® Michem® Guard 25 Nonionic, polyethylene dispersion
- Shakespeare S-3 Economy Nylon Copolymer Fishing Line, 30 lb
- Stellarchem DIOSHY® GP-935-UB2 TPE Compound
- Polyram PlusTek PB310G6 Nylon 6, 33% Glass Fiber
- ChevronTexaco HS Heating Fuel 2
- Barlog Plastics KEBAFORM C 6027 POM Copolymer, 30% mineral reinforced
Copyright © lookpolymers.com All Rights Reserved