Solvay Specialty Polymers Omnix® 4050 Polyamide, High Performance (HPPA) (Dry)
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Omnix® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Omnix® 4050 Polyamide, High Performance (HPPA) (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Omnix® 4050 is a 50% glass-fiber reinforced, high-performance polyamide (HPPA). It is particularly suited for replacing die-cast metal in a variety of mechanical applications and components used in automotive, consumer goods, E/E, and construction. Components injection molded from Omnix® 4050 display exceptional mechanical properties and excellent surface appearance even after moisture adsorption.Features: Fast Molding Cycle; Good Dimensional Stability; Good Impact Resistance; Good Surface Finish; High Flow; High Stiffness; High Strength; Hot Water Moldability; PaintableUses: Automotive Electronics; Electrical/Electronic Applications; Machinery Maintenance/RepairInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 245 MPa | 35500 psi | ISO 527-2 |
| Elongation at Break | 2.4 % | 2.4 % | ISO 527-2 |
| Tensile Modulus | 17.0 GPa | 2470 ksi | ISO 527-2 |
| Flexural Strength | 350 MPa | 50800 psi | ISO 178 |
| Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 90.0 kJ/m² | 42.8 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 11357-3 |
| Flammability, UL94 | HB @Thickness 0.800 mm |
HB @Thickness 0.0315 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 250 °C | 482 °F | |
| Front Barrel Temperature | 285 °C | 545 °F | |
| Melt Temperature | 275 - 290 °C | 527 - 554 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |
| Drying Temperature | 80.0 °C @Time 14400 - 43200 sec |
176 °F @Time 4.00 - 12.0 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Asia Pacific | |
| Europe | ||
| North America | ||
| Color | Black; Natural | |
| Form | Pellets | |
| Part Marking Code | >(PA+PPA)-GF50< | ISO 11469 |
| Processing Technique | Injection Molding; Water-Heated Mold Injection Molding | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Ineos Nova 1983 High Performance Styrenic Enhanced Polystyrene (discontinued **)
- Lord Adhesives Fusor® 309-1D / 309-2D Epoxy Adhesive
- Solvay Specialty Polymers Solef® 6020 Polyvinylidene Fluoride (PVDF)
- Special Metals DURANICKEL® 301 (UNS N03301) Spring Wire
- Unifrax Foamfrax® Isofoam Fiber Insulation
- Loctite® 3175 Acrylic Light Cure Adhesive
- EPICHEM Epicarb PC BLACK IQ Polycarbonate
- DSM Arnite® T08 200 (extrusion) T08 200 PBT (European and Asian Grade) (discontinued **)
- Karina 803-18/52-CR Gray PVC Compound
Copyright © lookpolymers.com All Rights Reserved