Solvay Specialty Polymers Ixef® 1521 Polyarylamide (PARA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyarylamide (PAA) , Polyarylamide, Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Ixef® 1521 Polyarylamide (PARA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ixef 1521 is a 50% glass-fiber reinforced, flame retardant polyarylamide which exhibits high strength and stiffness, outstanding surface gloss, and excellent creep resistance. - Natural: Ixef 1521/0008 - Black: Ixef 1521/9008 - Custom ColorableInjection Notes: Hot Runners: 250°C to 260°C (482°F to 500°F) Drying The material as supplied is ready for molding without drying. However, If the bags have been open for longer than 24 hours, the material needs to be dried. When using a desiccant air dryer with dew point of -28°C (-18°F) or lower, these guidelines can be followed: 0.5-1.5 hour at 120°C (248°F), 1-3 hours at 100°C (212°F), or 1-7 hours at 80°C (176°F). Injection Molding IXEF 1521 compound can be readily injection molded in most screw injection molding machines. A general purpose screw is recommended, with minimum back pressure. The measured melt temperature should be about 270°C (518°F), and the barrel temperatures should be around 250°C to 260°C (482°F to 500°F) in the rear zone, gradually increasing to 260°C to 280°C (500°F to 536°F) in the front zone. If hot runners are used, they should be set to 250°C to 260°C (482°F to 500°F). To maximize crystallinity, the temperature of the mold cavity surface must be held between 120°C and 140°C (248°F and 284°F). Molding at lower temperatures will produce articles that may warp, have poor surface appearance, and have a greater tendency to creep. Set injection pressure to give rapid injection. Adjust holding pressure and hold time to maximize part weight. Transfer from injection to hold pressure at the screw position just before the part is completely filled (95%-99%).Information provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.75 g/cc
0.0632 lb/in³
ISO 1183
Filler Content 50 %
50 %
Glass Fiber Reinforcement
Water Absorption 0.15 %

@Temperature 23.0 °C,
Time 86400 sec
0.15 %

@Temperature 73.4 °F,
Time 24.0 hour
ISO 62
Moisture Absorption at Equilibrium 1.3 %
1.3 %
65% RH; Internal Method
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm
0.0010 - 0.0030 in/in
Internal Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 230 MPa
33400 psi
ISO 527-2
Elongation at Break 1.9 %
1.9 %
ISO 527-2
Tensile Modulus 20.0 GPa
2900 ksi
ISO 527-2
Flexural Strength 340 MPa

@Temperature 23.0 °C
49300 psi

@Temperature 73.4 °F
ISO 178
Flexural Modulus 20.0 GPa
2900 ksi
ISO 178
Izod Impact, Notched 0.950 J/cm
1.78 ft-lb/in
ASTM D256
7.00 J/cm
13.1 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 17.0 µm/m-°C
9.44 µin/in-°F
ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
Unannealed; ISO 75-2/A
Flammability, UL94 V-0

@Thickness 0.750 mm
V-0

@Thickness 0.0295 in
Black; UL 94
V-0

@Thickness 1.50 mm
V-0

@Thickness 0.0591 in
All Colors; UL 94
5VA

@Thickness 1.50 mm
5VA

@Thickness 0.0591 in
Black; UL 94
Oxygen Index 32 %
32 %
ISO 4589-2
Glow Wire Test 900 °C

@Thickness 0.800 mm
1650 °F

@Thickness 0.0315 in
Glow Wire Ignition Temperature; IEC 60695-2-13
900 °C

@Thickness 3.00 mm
1650 °F

@Thickness 0.118 in
Glow Wire Ignition Temperature; IEC 60695-2-13
930 °C

@Thickness 1.50 mm
1710 °F

@Thickness 0.0591 in
Glow Wire Ignition Temperature; IEC 60695-2-13
960 °C

@Thickness 1.50 mm
1760 °F

@Thickness 0.0591 in
Glow Wire Flammability Index; IEC 60695-2-12
960 °C

@Thickness 3.00 mm
1760 °F

@Thickness 0.118 in
Glow Wire Flammability Index; IEC 60695-2-12
960 °C

@Thickness 0.800 mm
1760 °F

@Thickness 0.0315 in
Glow Wire Flammability Index; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 4.1

@Frequency 110 Hz
4.1

@Frequency 110 Hz
IEC 60250
Dielectric Strength 29.0 kV/mm
737 kV/in
IEC 60243-1
Dissipation Factor 0.012

@Frequency 110 Hz
0.012

@Frequency 110 Hz
IEC 60250
Comparative Tracking Index 400 V
400 V
IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 250 - 260 °C
482 - 500 °F
Front Barrel Temperature 260 - 290 °C
500 - 554 °F
Melt Temperature 270 °C
518 °F
Mold Temperature 120 - 140 °C
248 - 284 °F
Drying Temperature 120 °C
248 °F
Dry Time 0.500 - 1.50 hour
0.500 - 1.50 hour
Descriptive Properties Value Comments
Additive Flame Retardant
Agency Ratings FAA FAR 25.853a
Appearance Black
Colors Available
Natural Color
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Flame Retardant
Good Chemical Resistance
Good Creep Resistance
Good Dimensional Stability
High Flow
High Strength
Low Moisture Absorption
Outstanding Surface Finish
Ultra High Stiffness
Forms Pellets
Generic PARA
Injection Rate Fast
Processing Method Injection Molding
RoHS Compliance RoHS Compliant
Uses Aircraft Applications
Appliance Components
Appliances
Automotive Applications
Automotive Electronics
Automotive Under the Hood
Bushings
Business Equipment
Camera Applications
Furniture
Gears
Industrial Applications
Lawn and Garden Equipment
Machine/Mechanical Parts
Metal Replacement
Power/Other Tools